Search

Abstract: Yb:Y3Al5O12 (Yb:YAG) single crystals with Yb doping concentration 0.5at.%, 5at.%, 15at.%, 25at.%, 50at.%, 100at.% and Yb:YAlO3 (Yb:YAP) single crystals with Yb doping concentration 0.5at.%, 5at.%, 15at.%, 30at.% were grown by the Czochralski process. The fluorescence spectra of these crystals and the effects of self-absorption on the shape of the fluorescence spectra were studied. Through comparing the fluorescence spectra of Yb:YAG and Yb:YAP, all results indicate that the effects of self-absorption on the fluorescence spectra of Yb:YAP are remarkably stronger than that of Yb:YAG at the same Yb concentration. [Copyright &y& Elsevier]

Ho,Pr:CaYAlO 4 (Ho,Pr:CYA) crystal doped with 1 at.% Ho3+ and 0.1 at.% Pr3+ was successfully grown using the Czochralski method. Polarized absorption spectra, emission spectra, and fluorescence lifetime measurements were performed. The impact of Pr3+ co-doping on the ∼3 μm emission of Ho3+ ions was analyzed. The energy transfer efficiency from Ho3+:5I 7 to Pr3+:3F 2 energy level was calculated to be 60.66 %, indicating that Pr3+ effectively mitigated the self-termination effect in Ho,Pr:CYA crystals. The absorption cross-section at 645 nm was found to be 1.53 × 10−20 cm2 for σ polarization and 2.62 × 10−20 cm2 for π polarization. The emission cross-section at 2842 nm was calculated to be 0.86 × 10−20 cm2 for σ polarization and 1.33 × 10−20 cm2 for π polarization at 2908 nm, with a full width at half maximum (FWHM) of 139 nm and 88 nm, respectively. The fluorescence lifetimes of the 5I 6 and 5I 7 levels were measured to be 0.17 ms and 2.01 ms, respectively. These results collectively suggest that Ho,Pr:CYA crystals hold great potential as a candidate for 2.8 μm laser applications. • Ho3+,Pr3+ co-doped CaYAlO 4 crystal was grown by the Czochralski method. • The crystal structure, polarized absorption and emission spectra were investigated. • The intensity parameters were obtained using J-O theory. [ABSTRACT FROM AUTHOR]

Abstract We report on the growth, spectroscopic properties and visible laser operation of Pr3+-doped LaMgAl 11 O 19 (LMA) crystal. The absorption and emission spectra were recorded in visible wavelength range and the decay time of 3P 0 manifold was measured to be about 34.5 μs at room temperature. Using an InGaN laser diode as pump source, continuous-wave laser operation of Pr:LMA crystal have also been demonstrated in red at about 645 nm and deep red at about 725 nm, which provide new linearly polarized sources for various potential applications. Highlights • A Pr:LMA crystal was successfully gown by using the Czochralski method. • Spectral parameters of Pr:LMA crystal were obtained. • Using a blue laser diode as pump source, red and deep red laser were demonstrated from Pr:LMA crystal. [ABSTRACT FROM AUTHOR]

We report on the comparative growth and spectroscopy of Eu3+-doped Y 3 Al 5 O 12 (YAG) and Y 3 ScAl 4 O 12 crystals grown by the micro-pulling-down (μ-PD) method. The structure of the as-grown crystals was determined by X-ray diffraction (XRD) and Raman spectroscopy. The absorption spectra of the crystals are dominated by a strong line centered at 395 nm, matching well with the emission of commercial ultraviolet laser diodes. The Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals exhibit strongest red emission centered at 710 nm and the full width at half maximum (FWHM) was calculated to be 2.03 and 3.19 nm, respectively. The fluorescence decay curves of 5D 0 levels were measured and discussed. All the results indicate that the Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals are promising candidates for red luminescent/laser materials. • Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals were successfully grown by the micro-pulling-down technique for the first time. • The structure parameters of Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals were investigated by XRD. • Spectral parameters of Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals were obtained and compared. [ABSTRACT FROM AUTHOR]