We report laser operation of two Tb3+-activated gain media, Tb:LiYF4 and LiTbF4, in yellow or/and green spectral region. A record-high slope efficiency of 63% among Tb3+-lasers and maximum output power of 1.17 W (incident power of 2.79 W) at around 544 nm were obtained with a c-cut 15%Tb:LiYF4 crystal. The yellow laser characteristics in σ-polarization were studied. A slope efficiency of 21% at 582 nm was achieved. More importantly, we succeeded in laser operation of LiTbF4 for the first time to the best of our knowledge. Laser oscillation at around 544 nm yielded a maximum slope efficiency of 45%. This points toward the possibility of producing high-energy pulsed lasers using LiTbF4, which features a high active-ion concentration as well as relatively long lifetime.

We report laser operation of Pr:YAlO3 pumped by a frequency-doubled optically pumped semiconductor laser. Continuous-wave laser oscillations at around 622 nm, 662 nm, and 747 nm were demonstrated in plano-concave or/and plano-plano cavities. The maximum slope efficiencies were found to be 37%, 35%, and 59%, respectively, which are record-high values for Pr:YAlO3 lasers. Furthermore, lasing at 622 nm was demonstrated at room temperature for the first time to the best of our knowledge.

Efficient room-temperature laser operation was obtained in the wavelength range from 2117 nm to 2134 nm with Ho:Lu(2)O(3) and Ho:Y(2)O(3) as the active materials. With an FBG-stabilized Tm-doped fiber laser as the pump source, the maximum slope efficiency and output power of the Ho:Y(2)O(3) laser were 63% and 18.8 W, respectively. With Ho:Lu(2)O(3) the respective values were 76% and 25.2 W. With Ho:Sc(2)O(3) as the active material the accessible wavelength range could be expanded to 2158 nm in a diode-pumped setup.

In this work we report the spectroscopy and laser results of several Thulium doped BaY(2)F(8) single crystals grown using the Czochralski technique. The doping concentration is between 2at.% and 18at.%. We performed room temperature laser experiments pumping the samples with a laser diode at 789 nm obtaining 61% as maximum optical-to-optical efficiency with a maximum output power of 290 mW and a minimum lasing threshold of 26 mW. The lasing wavelength changed with the dopant concentration from 1927 nm up to 2030 nm and the nature of the transition changed from purely electronic to vibronic, accordingly.