Search

The structural and superconducting properties of alkali-Bi-based compounds, KBi2 and RbBi2, were investigated over a wide pressure range for the first time. The samples of KBi2 and RbBi2 were prepared using a liquid ammonia (NH3) technique, and demonstrated superconductivity with superconducting transition temperatures, Tc, of 3.50 and 4.21 K at ambient pressure, respectively. The onset superconducting transition temperature, Tconset, of KBi2 decreased slightly; however, it suddenly jumped at 2 GPa and increased gradually with pressure, indicating the presence of two superconducting phases in the low-pressure range. The pressure-dependent X-ray diffraction patterns indicate that the KBi2 sample decomposed into KBi and Bi at pressures higher than 2.5 GPa. Moreover, a discontinuous change in Tconset was observed for KBi2 at 9 GPa, which reflects the decomposition of KBi2 into KBi and Bi. By contrast, the value of Tconset of RbBi2 was almost constant over a pressure range of 0–8 GPa. Thus, the superconducting properties and stability of alkali-Bi-based compounds against pressure were comprehensively explored in this study. In addition, the superconducting Cooper pair symmetry was investigated from the magnetic field dependence of Tc of KBi2 at 0.790 and 2.32 GPa, and of RbBi2 at 1.17 GPa, indicating the exact deviation from the simple s-wave paring model, which may be due to the complex electronic structure of Bi. The results elucidated the exotic superconducting properties of KBi2 and RbBi2 based on the pressure and magnetic field dependence of Tc and verified the chemical stability of KBi2 under pressure. [ABSTRACT FROM AUTHOR]

Laying-down gold nanorods (GNRs) of a monolayer immobilized on a solid substrate was realized with a hybrid method, a combination of three elemental technologies: surface modification, electrophoresis, and solvent evaporation. The self-assembly of CTAB-protected GNRs in the solution was induced by 0.05 mM of EDTA. The assembled GNRs were deposited in a laying-down form on the solid surface during the hybrid method. The final coverage was over 71% on the substrate with an area larger than 0.6 cm2. The spacing between the sides of the GNRs was fixed to be 4.6 ± 0.9 nm by the thermal annealing-promoted crystalline packing of the bilayer of CTAB salt-bridged with EDTA. The obtained laying-down GNRs of a monolayer on the gold substrate show a small shift of the transverse LSPR around 550–570 nm (with a width of around 100 nm) and a large red shift of the longitudinal LSPR to be 900–1050 nm (with a width of 500 nm), because of the strong electromagnetic coupling between the GNRs and gold substrate. Therefore it can be used in a wide range of wavelengths for surface enhanced Raman spectroscopy (SERS) applications. The film has a high enhancement factor with 105 for R6G. [ABSTRACT FROM AUTHOR]

Herein, we report the preparation and characterization of BaBi3 clarified by DC magnetic susceptibility, powder X-ray diffraction (XRD), and electrical transport. The superconducting properties of BaBi3 were elucidated through the magnetic and electrical transport properties in a wide pressure range. The superconducting transition temperature, Tc, showed a slight decrease (or almost constant Tc) against pressure up to 17.2 GPa. The values of the upper critical field, Hc2, at 0 K, were determined to be 1.27 T at 0 GPa and 3.11 T at 2.30 GPa, using the formula, because p-wave pairing appeared to occur for this material at both pressures, indicating the unconventionality of superconductivity. This result appears to be consistent with the topological non-trivial nature of superconductivity predicted theoretically. The pressure-dependent XRD patterns measured at 0–20.1 GPa indicated no structural phase transitions up to 20.1 GPa, i.e., the structural phase transitions from the α phase to the β or γ phase which are induced by an application of pressure were not observed, contrary to the previous report, demonstrating that the α phase is maintained over the entire pressure range. Admittedly, the lattice constants and the volume of the unit cell, V, steadily decrease with increasing pressure up to 20.1 GPa. In this study, the plots of Tcversus p and V versus p of BaBi3 are depicted over a wide pressure range for the first time. [ABSTRACT FROM AUTHOR]

A new superconducting sample, BaTi2Bi2O, was synthesized and characterized over a wide pressure range. The superconducting transition temperature, Tc, of BaTi2Bi2O was 4.33 K at ambient pressure. The crystal structure was tetragonal (space group of P4/mmm (No. 123)), according to the X-ray diffraction (XRD) pattern at ambient pressure. The XRD pattern was analyzed using the Le Bail method. The magnetic-field dependence of the magnetization at different temperatures was precisely investigated to elucidate the characteristics of the superconductivity. The pressure-dependent XRD patterns showed absence of structural phase transitions up to 19.8 GPa. The superconducting properties of BaTi2Bi2O were investigated under pressure. Tc monotonously increased with the pressure (p) up to 4.0 GPa and saturated above 4.0 GPa. The variations in the Tc–p plot were thoroughly analyzed. The Cooper pair symmetry (or superconducting pairing mechanism) was analyzed based on the magnetic field dependence of the superconductivity at ambient and high pressures, which indicated a sign of p-wave pairing for the superconductivity of BaTi2Bi2O, i.e., topologically nontrivial sign was suggested for BaTi2Bi2O. [ABSTRACT FROM AUTHOR]