Search

Combinations of fluorinated and silicone based elastomers were elaborated through the in situ synthesis of interpenetrating polymer networks (IPNs). The PDMS network was formed by dibutyltindilaurate catalyzed addition between the hydroxy end groups of α,ω-(3-hydroxypropyl)polydimethylsiloxane (PDMS) and a pluriisocyanate cross-linker. The poly(fluorinated acrylate) (polyAcRf6) network was obtained from free-radical copolymerization of a fluorinated acrylate with ethylene glycol dimethacrylate in the presence of dicyclohexyl peroxydicarbonate as the initiator. IPNs with different relative weight proportions of the fluorinated vs silicone partners were characterized by DMTA and DSC. Density refractive index and contact angle measurements reveal a satisfactory interpenetration degree of PDMS and polyAcRf6 networks. In addition, these materials present an unusual variation of density values and of the surface properties as a function of the relative weight composition.

Interpenetrating polymer networks combining cellulose acetate butyrate (CAB) and α,ω-divinyl-polydimethylsiloxane (PDMS) in different weight proportions have been synthesized. The synthesis involves a one pot–one shot process in which all components are first mixed together. For each composition, the relative CAB and PDMS network formation rates are adjusted through the concentration of DBTDL used as CAB network formation catalyst. Thus, the chemically independent networks are formed quasi-simultaneously in order to avoid phase separation. The CAB cross-linking density effect on the PDMS/CAB IPN mechanical properties has also been particularly studied. All synthesized IPNs are transparent and only one mechanical relaxation temperature lying between those of the single CAB and PDMS networks is observed by DMTA analysis. These results show that the networks are correctly interpenetrated and no phase separation is observed at the DMTA level. Some mechanical properties of the PDMS network are significantly improved in this IPN combination and their stress–strain behavior has highlighted a synergistic effect arising from the IPN architecture. Thus, these IPNs exhibit many characteristics, which would allow defining them as close to ‘true’ IPNs.

In order to improve polyisobutene (PIB) mechanical properties, a PIB network is combined with a polystyrene (PS) one into an interpenetrating polymer network (IPN) architecture. PIB network is formed by alcohol addition between the hydroxyl end groups of a telechelic dihydroxy-polyisobutene and a pluri-isocyanate. PS network is synthesized by free-radical copolymerization of styrene with divinylbenzene. Thus, the optimal synthesis conditions are determined by FTIR spectroscopy and the kinetics of the alcohol–isocyanate addition is studied in detail. A short kinetic study of the PS network formation inside the PIB network is also carried out. The highest degree of interpenetration is obtained by forming the PIB network first. The corresponding transparent IPNs exhibit two mechanical relaxations corresponding to those of PS and PIB enriched phases. However, mechanical properties of PIB networks are tremendously improved by the presence of a PS network in such IPN architectures.

The synthesis of an interpenetrating polymer network (IPN) combining a polydimethylsiloxane (PDMS) network and a cellulose acetate butyrate (CAB) network is reported. The silicone network is formed through a thiol-ene addition between α,ω-divinyl-poly(dimethylsiloxane) and trimethylolpropane tris(3-mercaptopropionate) as a cross-linking agent. The CAB network is synthesized by pluri-isocyanate cross-linking through dibutyltindilaurate (DBTDL) catalysis. The IPN is prepared through a one pot-one shot process. Kinetic studies of the IPN synthesis showed that some thiol cross-linking functions react with DBTDL which slows down the CAB network formation by decreasing the available quantity of DBTDL catalyst. Thus, in order to obtain a transparent material withstanding the presence of thiol groups, the DBTDL content must be increased and the resulting IPN exhibits then only one transition temperature as measured by dynamic thermomechanical analysis witnessing a high level of interpenetration.

Polycarbonates (PC) are currently used for organic optical glass; nevertheless they show a poor impact resistance which may be increased by combination with cellulose acetate butyrate (CAB) into a PC/CAB interpenetrating polymer network (IPN), without altering the material transparency as we show here. A series of rigid IPNs based on an aliphatic polycarbonate and CAB was prepared through in situ polymerization techniques. The kinetics of the formation of two networks in the IPNs were studied by FTIR spectroscopy. Effects of the CAB cross-linking and weight proportions of the two components in the IPNs were investigated by dynamic mechanical thermal analysis.