This study reveals the impact resistance of shear thickening gel (STG) impregnated four‐layer regular angle interlocking fabrics (AIF) composites. The effects of STG parameters, including reaction time, reaction temperature, and reaction ratio, on the rheological characterization and mechanical properties of STG/AIF flexible composites were investigated. The results show that the increase in STG parameters accelerated the formation of BO crosslink bonds within the STG. The energy storage modulus of STG increased by three orders of magnitude for a reaction temperature of 230°C, a reaction time of 9 h, and a reaction ratio of 12.5%. STG had an obvious shear thickening effect. The coupling effect of STG and AIF increases the inter‐yarn friction. The shear thickening effect of STG and the deformation of AIF fabric synergistically absorbed the impact energy, and the energy absorption rate reached 95.6%. The material surface was not significantly damaged after the low‐velocity impact. The STG/AIF flexible composites showed excellent impact energy absorption properties. Highlights: A new high‐energy absorption and impact resistance composite was prepared.Increased STG reaction ratio and temperature promoted its internal reaction.B and O atomic interactions enhance the rheological properties of STG.STG and fabric synergistically improve the impact resistance. [ABSTRACT FROM AUTHOR]

This work reveals the synergistic effect of argon/nitrogen double plasma alteration on the mechanical properties of para‐aramid fiber/epoxy resin composites with various laminating sequences. Acoustic emission monitored interface failure during tensile, bending and fracture testing. A comparative analysis was conducted on the bending performance of the composites modified by argon/nitrogen double plasma and single plasma. The results showed that the synergistic effect of nitrogen and high‐energy molecule argon optimized the modifying effect of argon/nitrogen double plasma. The optimal modification parameters obtained through fiber extraction testing analysis are power 200 W, time 120 s, and Ar/N2 double gas flow rate of 12 sccm. After plasma treatment, twill weave modifies better than plain weave. The AE signal amplitude of PX1 is minimized during stretching. Due to the difference in internal bending stiffness of PX2, interface delamination failure is more likely to occur. The PX5 had greater fiber and matrix debonding failure between mode‐II fracture tests due to the weak modification effect of plain weave and its difficulty in deformation. In ballistic testing, PX1 blocks impact force through fiber bundle stretching deformation, while PX4 is more brittle. Highlights: Prepare para‐aramid/epoxy resin composites with various laminating sequences.Study on the interfacial properties of composites treated with double plasma.The composites with different gas sources treatment were analyzed.Acoustic emission analysis was used to identify interface failure modes.The bonding strength between plain and plain interfaces is the lowest. [ABSTRACT FROM AUTHOR]