Search

Wood plastic composite (WPC) usage and demand have increased because of its interesting chemical and mechanical properties compared to other plastic materials. However, there is a possibility of structural and mechanical changes to the material when exposed to the external environment; most research on wood plastic is performed on the material with elevated fiber content (40–70%). Therefore, more research needs to be performed regarding these issues, especially when the fiber content of the WPC is low. In this study, composite materials composed of high-density polyethylene (HDPE) reinforced with yellow birch fibers (20 and 30%) were made by injection molding. The fibers were treated with dissolved zinc oxide (ZnO) powder in sodium oxide (NaOH) solution, and the fabricated material was exposed to fungal rot. ZnO treatment in this case is different from most studies because ZnO nanoparticles are usually employed. The main reason was to obtain better fixation of ZnO on the fibers. The mechanical properties of the composites were assessed by the tensile and Izod impact tests. The impact energies of the samples fabricated with ZnO-treated fibers and exposed to Gloephyllum trabeum and Trametes versicolor decreased, when compared to samples fabricated with ZnO-nontreated fibers. The mechanical properties of the samples composed of ZnO-treated fibers and exposed to rot decreased, which were reported by a decreased Young’s modulus and impact energies. The usage of ZnO treatment prevented mycelium proliferation, which was nonexistent on the samples. It has been noted that the decrease in mechanical properties of the treated samples was because of the action of NaOH used to dissolve the ZnO powder.

In this work, laminated polyester thermoset composites based on palm tree fibers extracted from palms leaflets and glass mats fibers were manufactured to develop hybrid compositions with good mechanical properties; the mixture of fibers was elaborated to not exceed 25 vol.%. Samples were prepared with a resin transfer molding (RTM) method and mechanically characterized using tensile and flexural, hardness, and impact tests, and ultrasonic waves as a non-destructive technique. The water sorption of these composite materials was carried out in addition to solar irradiation aging for approximately 300 days to predict the applicability and the long-term performance of the manufactured composites. Results have shown that the use of glass fibers significantly increased all properties; however, an optimum combination of the mixture could be interesting and could be developed with less glass sheet and more natural fibers, which is the goal of this study. On the other hand, exposure to natural sunlight deteriorated the mechanical resistance of the neat resin after only 60 days, while the composites kept high mechanical resistance for 365 days of exposure.

Wood–plastic composites have emerged and represent an alternative to conventional composites reinforced with synthetic carbon fiber or glass fiber–polymer. A wide variety of wood fibers are used in WPCs including birch fiber. Birch is a common hardwood tree that grows in cool areas such as the province of Quebec, Canada. The effect of the filler proportion on the mechanical properties, wettability, and thermal degradation of high-density polyethylene/birch fiber composite was studied. High-density polyethylene, birch fiber and maleic anhydride polyethylene as coupling agent were mixed and pressed to obtain test specimens. Tensile and flexural tests, scanning electron microscopy, dynamic mechanical analysis, differential scanning calorimetry, thermogravimetry analysis and surface energy measurement were carried out. The tensile elastic modulus increased by 210% as the fiber content reached 50% by weight while the flexural modulus increased by 236%. The water droplet contact angle always exceeded 90°, meaning that the material remained hydrophobic. The thermal decomposition mass loss increased proportional with the percentage of fiber, which degraded at a lower temperature than the HDPE did. Both the storage modulus and the loss modulus increased with the proportion of fiber. Based on differential scanning calorimetry, neither the fiber proportion nor the coupling agent proportion affected the material melting temperature.

Numerical modeling of the thermoforming process of polymeric sheets requires precise knowledge of the viscoelastic behavior under conjugate effect pressure and temperature. Using two different experiments, bubble inflation and dynamic mechanical testing on a high-density polyethylene (HDPE) nanocomposite reinforced with polymethylsilsesquioxane HDPE (PMSQ–HDPE) nanoparticles, material constants for Christensen’s model were determined by the least squares optimization. The viscoelastic identification relative to the inflation test seemed to be the most appropriate for the numerical study of thermoforming of a thin PMSQ–HDPE part. For this purpose, the finite element method was considered.