In this paper, the obtaining and characterization of five experimental models of novel polymer composite materials with ferrite nano-powder are presented. The composites were obtained by mechanically mixing two components and pressing the obtained mixture on a hot plate press. The ferrite powders were obtained by an innovative economic co-precipitation route. The characterization of these composites consisted of physical and thermal properties: hydrostatic density, scanning electron microscopy (SEM), and TG DSC thermal analyses, along with functional electromagnetic tests in order to demonstrate the functionality of these materials as electromagnetic shields (magnetic permeability, dielectric characteristics, and shielding effectiveness). The purpose of this work was to obtain a flexible composite material, applicable to any type of architecture for the electrical and automotive industry, necessary for protection against electromagnetic interference. The results demonstrated the efficiency of such materials at lower frequencies, but also in the microwave domain, with higher thermal stability and lifetime.

In this work, improved fracture toughness of tetra-functional epoxy polymer was obtained using two-dimensional (2H polytype) molybdenum disulfide (MoS2) nano-platelets as a filler. Simultaneous in-situ exfoliation and functionalization of MoS2 were achieved in the presence of cetyltrimethylammonium bromide (CTAB) via sonication. The aim was to improve the dispersion of MoS2 nanoplatelets in epoxy and enhance the interfacial interaction between nanoplatelets and epoxy matrix. Epoxy nanocomposites with CTAB functionalized MoS2 (f-MoS2) nanoplatelets, ranging in content from 0.1 wt% up to 1 wt%, were fabricated. Modified MoS2 improved the fracture properties (81%) of tetrafunctional epoxy nanocomposites. The flexural strength and compressive strength improved by 64% and 47%, respectively, with 0.25 wt% loading of f-MoS2 nanoplatelets compared to neat epoxy. The addition of f-MoS2 nanoplatelets enhanced the thermomechanical properties of epoxy. This work demonstrated the potential of organically modified MoS2 nanoplatelets for improving the fracture and thermal behavior of tetrafunctional epoxy nanocomposites.