Search

The thermal decomposition of the thermodynamic, kinetic and mechanisms of copolymer P(DAC-AM) samples with serial cationicity and intrinsic viscosity ([η]), and the control samples of homopolymer PAM and PDAC, were studied and analyzed using TG, DSC, FTIR. The results of the thermal decomposition thermodynamics confirmed that the thermal decomposition processes of the serial P(DAC-AM) samples and the two control samples could be divided into two stages. It was found that the processes of the copolymer P(DAC-AM) samples were not a simple superposition of those of homopolymers, whose monomers had composed the unit structures of the copolymer, but there were interactions between the two suspension groups. The results of thermal decomposition kinetics showed that the apparent activation energy (E) of the thermal decomposition process of all polymer samples had different varying trends in the terms of weight-loss rate (α). The reaction order (n) of the thermal decomposition of P(DAC-AM) in Stage I and II was close to 1, but in the former and the latter it tended to be 2 and 0.5, respectively. Finally, the thermal decomposition mechanism of copolymer P(DAC-AM) samples was discussed. The above research could not only fill in the knowledge vacancy of the thermal decomposition of the thermodynamic, kinetic and mechanisms of P(DAC-AM), but could also lay a foundation for the study of thermal decomposition mechanisms of the other types of polymers, including cationic polymers. [ABSTRACT FROM AUTHOR]

Poly(3-methacrylamido propyl trimethyl ammonium chloride) (PMAPTAC) is a typical cationic water-soluble polyelectrolyte, which has been widely used in petroleum, papermaking, daily cosmetics and other fields in the form of an aqueous solution. However, the acid–base and thermal stability of PMAPTAC in aqueous solution have not been reported yet, which hinders its further application in high-temperature and acid–base environments. To address these deficiencies, the effects of temperature and pH of PMAPTAC with different intrinsic viscosities on its hydrolysis stability were investigated qualitatively and quantitatively, and the hydrolysis mechanism was studied. Firstly, the qualitative analysis showed that the apparent viscosity of the PMAPTAC solution decreased with hydrolysis time at different temperatures and pH. The higher the temperature and the lower the pH, the greater the viscosity loss of PMAPTAC. The quantitative analysis showed that the hydrolysis rate of the PMAPTAC sample solution increased with the increase in temperature and pH. In addition, the intrinsic viscosity of PMAPTAC samples had little effect on the hydrolytic stability of PMAPTAC. Secondly, by analyzing the viscosity curves at different pH and temperatures by Arrhenius analysis, the Arrhenius equations were found to be 1/τ = 200.34e^((−25.04)/RT), 1/τ = 9127.07e^((−38.90)/RT) and 1/τ = 4683.03e^((−39.89)/RT) for pH 3, pH 7 and pH 11, respectively. Thirdly, the hydrolysis rate of PDMC was the fastest under alkaline conditions. In addition, compared with PDMC, PMAPTAC had better hydrolysis stability under the same conditions. Finally, the mechanism of the hydrolyzed polymer was studied by FTIR and 13CNMR, which showed that the carbonyl group of PMAPTAC was hydrolyzed into a carboxyl group, and the small molecule (3-aminopropyl) trimethylammonium chloride was generated, while the ester group of PDMC was hydrolyzed into a carboxyl group, and choline chloride was released. The above results can provide a theoretical basis for the application of PMAPTAC in some high-temperature and acid–base environments. [ABSTRACT FROM AUTHOR]