In this study, the effect of plasma treatment on glass-cloth-containing polytetrafluoroethylene (GC–PTFE) was investigated. Previous plasma studies investigated pure PTFE (which does not contain glass cloth) but not GC–PTFE. The effect of Ar + H2O plasma treatment on GC–PTFE was investigated. The Ar + H2O plasma-treated GC–PTFE sheets were thermally compressed to stainless steel (SUS304) foils without using adhesive, and the GC–PTFE/SUS304 adhesion strengths were measured using a 90° peel test. The adhesion strength increased with the increase in the plasma treatment time (0.8 and 1.0 N/mm at 20 s and 300 s, respectively). Thus, strong adhesion between GC–PTFE/SUS304 was achieved without adhesive. This improvement in the adhesion properties of GC–PTFE can be attributed to the generation of oxygen-containing functional groups and the decrease in the surface roughness of the samples. Thereafter, the adhesion properties of GC–PTFE and pure PTFE were compared. Because, unlike pure PTFE, GC–PTFE has no weak boundary layer, GC–PTFE exhibited better adhesion properties than pure PTFE under short plasma treatment times. [ABSTRACT FROM AUTHOR]

Heat-assisted plasma (HAP) treatment using He gas is known to improve the adhesive-bonding and adhesive-free adhesion properties of polytetrafluoroethylene (PTFE). In this study, we investigated the effects of He and Ar gaseous species on the HAP-treated PTFE surface. Epoxy (EP) adhesive-coated stainless steel (SUS304) and isobutylene–isoprene rubber (IIR) were used as adherents for the evaluation of the adhesive-bonding and adhesive-free adhesion properties of PTFE. In the case of adhesive bonding, the PTFE/EP-adhesive/SUS304 adhesion strength of the Ar-HAP-treated PTFE was the same as that of the He-HAP-treated PTFE. In the case of adhesive-free adhesion, the PTFE/IIR adhesion strength of the Ar-HAP-treated PTFE was seven times lower than that of the He-HAP-treated PTFE. The relation among gaseous species used in HAP treatment, adhesion properties, peroxy radical density ratio, surface chemical composition, surface modification depth, surface morphology, surface hardness, and the effect of irradiation with vacuum ultraviolet (VUV) and UV photons were investigated. The different adhesive-free adhesion properties obtained by the two treatments resulted from the changes in surface chemical composition, especially the ratios of oxygen-containing functional groups and C–C crosslinks. [ABSTRACT FROM AUTHOR]