This paper describes the synthesis of NIPU by using cardanol as starting material. A cardanol formaldehyde oligomer was first prepared through the reaction of cardanol and formaldehyde, catalyzed by citric acid. The resulting oligomer was then subjected to epoxidation with m-chloroperbenzoic acid to obtain an epoxide compound, which was subsequently used to fix carbon dioxide (CO2) and form a cyclic carbonate. Using this cyclic carbonate, along with an amine, cardanol-based isocyanate polyurethane (NIPU) was prepared. Different characterization methods, such as Fourier transform infrared spectroscopy (FTIR), proton nuclear magnetic resonance (NMR), gel permeation chromatography (GPC), and thermogravimetric analysis (TGA), were used to confirm the synthesis of the four intermediate products and NIPU in the reaction process. This study highlights the promise of bio-based NIPU as a sustainable alternative in a number of applications while offering insightful information on the synthesis and characterization of the material. [ABSTRACT FROM AUTHOR]

In this work, poly (vinylidene fluoride) (PVDF) hierarchically porous membranes (HPMs) with isolated large pores and continuous narrow nano-pores have been fabricated from its blend with poly (methyl methacrylate) (PMMA) based on the combination of crystallization template with chemical or supercritical CO2 foaming. On the one hand, the decomposition of azodicarbonamide (ADC, chemical foaming agent) or the release of CO2 can produce isolated large pores. On the other hand, PMMA is expelled during the isothermal crystallization of PVDF in their miscible blend, yielding narrow nano-pores upon etching with a selective solvent. In the case of supercritical CO2, the attained PVDF HPMs fail to improve separation performance because of the compact wall of isolated-large-pore and consequent poor connectivity of hierarchical pores. In the case of ADC, the optimal HPM exhibits much higher flux (up to 20 times) without any loss of selectivity compared with the reference only with nano-pores. The enhanced permeability can be attributed to the shorter diffusion length and lower diffusion barrier from isolated large pores, while the comparable selectivity is determined by narrow nano-pores in THE matrix. [ABSTRACT FROM AUTHOR]