The melt blending of polylactic acid (PLA) and thermoplastic silicone polyurethane (TPSiU) elastomer was performed to toughen PLA. The molecular structure, crystallization, thermal properties, compatibility, mechanical properties and rheological properties of the PLA/TPSiU blends of different mass ratios (100/0, 95/5, 90/10, 85/15 and 80/20) were investigated. The results showed that TPSiU was effectively blended into PLA, but no chemical reaction occurred. The addition of TPSiU had no obvious effect on the glass transition temperature and melting temperature of PLA, but slightly reduced the crystallinity of PLA. The morphology and dynamic mechanical analysis results demonstrated the poor thermodynamic compatibility between PLA and TPSiU. Rheological behavior studies showed that PLA/TPSiU melt was typically pseudoplastic fluid. As the content of TPSiU increased, the apparent viscosity of PLA/TPSiU blends showed a trend of rising first and then falling. The addition of TPSiU had a significant effect on the mechanical properties of PLA/TPSiU blends. When the content of TPSiU was 15 wt%, the elongation at break of the PLA/TPSiU blend reached 22.3% (5.0 times that of pure PLA), and the impact strength reached 19.3 kJ/m2 (4.9 times that of pure PLA), suggesting the favorable toughening effect. [ABSTRACT FROM AUTHOR]

High molecular weight poly (p-phenylene-terephthalamide) (h-PPTA) was blended with the commercial PPTA in concentrated sulfuric acid to improve the spinnability of the polymer solutions and the mechanical properties of the as-spun fibers. h-PPTA in the solution has an influence on the temperature of the formation of liquid crystalline phenomenon. The temperature range with the existence of the liquid crystalline phase increases upon the contents of h-PPTA in the solution, and the extended temperature window is helpful for the preparation of PPTA fibers by the dry-jet wet-spinning technology. The long-chains of h-PPTA enhance the inter-macromolecular interactions and induce the orientation of short-chains for PPTA along the fiber axis under the shear stress in the spinneret and the stretching stress at the air gap. These effects also increase the maximum drawing ratio in the spinning process and improve the mechanical properties of the obtained fibers. The crystallinity and crystal orientation of the fibers are investigated by X-ray diffraction, and results from sonic velocity test further confirm ordering state of the macromolecular chains. The fibril morphologies of the fibers are also studied by a scanning electric microscope. [ABSTRACT FROM AUTHOR]

Poor interfacial bonding between stainless steel wire and the inner and outer layer resin matrix significantly affects the mechanical performance of braid-reinforced composite hollow fiber tube, especially torsion control. In this work, a coating of thermoplastic polyurethane (TPU) deposited on the surface of stainless steel wire greatly enhanced the mechanical performance of braid-reinforced composite hollow fiber tube. This method takes advantage of the hydrogen bonding between polyether block amide (PEBA) and thermoplastic polyurethane (TPU) for surface modification of stainless steel wire, as well as the good compatibility between PEBA and TPU. The mechanical properties of composited tubes demonstrate that the interlaminar shear strength, modulus of elasticity, and torque transmission properties were enhanced by 27.8%, 42.1%, and 41.4%, respectively. The results indicating that the interfacial adhesion between the coated stainless steel wire and the inner and outer matrix was improved. In addition, the interfacial properties of composite hollow fiber tube before and after coating was characterized by the optical microscope, and results show that the interfacial adhesion properties of the modified stainless steel wire reinforced resin matrix composites were greatly improved. [ABSTRACT FROM AUTHOR]

Aramid fibers with low density and high strength, modulus, and thermal resistance are widely used in applications such as bulletproof vests and cables. However, owing to their chemical structure, they are sensitive to ultraviolet light, which degrades the fibers' useful mechanical properties. In this study, titanium dioxide (TiO2) nanoparticles were synthesized both on the aramid III fiber surface and in the interfacial space between the fibrils/microfibrils in supercritical carbon dioxide (scCO2) to improve the UV resistance of aramid fibers. The effects of scCO2 treatment pressure on the TiO2 structure, morphology, surface composition, thermal stability, photostability, and mechanical properties were investigated using Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, thermogravimetric analysis, ultraviolet–visible spectroscopy, and single-fiber test. The results show that amorphous TiO2 formed on the fiber surface and the interface between fibrils/microfibrils, and decreased the photodegradation rate of the aramid III fiber. Moreover, this modification can also improve the tensile strength via treatment at low temperature and without the use of a solvent. The simple synthesis process in scCO2, which is scalable, is used for mild modifications with a green solvent, providing a promising technique for synthesizing metal dioxide on polymers. [ABSTRACT FROM AUTHOR]

Aramid fibers (AFs) with their high Young′s modulus and tenacity are easy to degrade seriously with ultraviolet (UV) radiation that leads to reduction in their performance, causing premature failure and limiting their outdoor end use. Herein, we report a method to synthesize nano-SiO2 on AFs surfaces in supercritical carbon dioxide (Sc-CO2) to simultaneously improve their UV resistance, thermal stability, and interfacial shear strength (IFSS). The effects of different pressures (10, 12, 14, 16 MPa) on the growth of nanoparticles were investigated. The untreated and modified fibers were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). It was found that the nano-SiO2-decorated fibers exhibited improvement of thermal stability and mechanical properties, and the IFSS of the nano-SiO2 modified fibers increases by up to 64% compared with the untreated fibers. After exposure to 216 h of UV radiation, the AFs-UV shows a less decrease in tensile strength, elongation to break and tensile modulus, retaining only 73%, 91%, and 85% of the pristine AFs, respectively, while those of AFs-SiO2-14MPa-UV retain 91.5%, 98%, and 95.5%. In short, this study presents a green method for growing nano-SiO2 on the surface of AFs by Sc-CO2 to enhance the thermal stability, IFSS, and UV resistance. [ABSTRACT FROM AUTHOR]

High modulus aramid fiber, such as Kevlar 49, is conventionally prepared by the heat annealing of high strength aramid fiber under a suitable tension at high temperature, especially higher than 500 °C. This enables the mobility of a rigid molecule chain to be rearranged into a more perfect crystalline or orientation structure under tension. However, annealing decreases the tensile strength, since the thermal degradation of the molecular chain at high temperature cannot be avoided. Kevlar 49 fibers treated in supercritical carbon dioxide (scCO2) under tension could improve their mechanical properties at a low temperature. The effects of the tension on the mechanical properties and structure of the Kevlar 49 fibers were studied by mechanical testing, wide-angle and small-angle X-ray scattering (WAXS, SAXS), and scanning electron microscopy (SEM). The results show that the mechanical properties, crystallinity and orientation of the fiber can be improved when the tension is less than 0.6 cN/dtex, which may be due to the increasing of the mobility of a rigid segment with the help of the plasticization of scCO2 and re-arrangement of macromolecular chain into crystalline and orientation structure under tension. What's more, the amorphous region also was enhanced by crosslinking reaction of toluene 2,4-diisocyanate (TDI) with the chain end groups of the macromolecules in the amorphous regions. However, a decrease of tenacity was found when the tension was higher than 0.6 cN/dtex, which is because the tension was so high that the microfibril was broken. The results indicated that treating the Kevlar 49 fiber in scCO2 under a suitable tension with TDI as a crosslink agent can simultaneously improve both the tenacity and modulus of the fiber. [ABSTRACT FROM AUTHOR]

Polylactic acid (PLA) is one of the most promising bio-based materials, but its inherent hydrophobicity limits its application. Although nanocellulose (NCC) is a desirable reinforcement for PLA, the poor interface compatibility between the two has been a challenge. In this work, hydroxyapatite (HAP) modified NCC was prepared, and the obtained NCC/HAP reinforcement was used to prepare PLA/NCC-HAP composites. Different ratios of NCC to HAP were studied to explore their effects on the mechanical and thermodynamic properties of the composites. When the ratio of NCC to HAP was 30/70, the tensile strength and tensile modulus of the composite film reached 45.6 MPa and 2.34 GPa, respectively. Thermogravimetric analysis results indicate that thermal stability of the composites was significantly improved compared with pure PLA, reaching 346.6 °C. The above revelations show that NCC/HAP significantly improved the interface compatibility with PLA matrix. [ABSTRACT FROM AUTHOR]

In order to obtain F-III fibers with high mechanical properties, pristine F-III fibers were hot drawn at the temperature of 250 °C, pressure of 14 MPa, tension of 6 g·d−1, and different times, which were 15 min, 30 min, 45 min, 60 min, 75 min, 90 min, and 105 min, respectively, in supercritical carbon dioxide (Sc-CO2) in this article. All the samples, including the pristine and treated F-III fibers, were characterized by a mechanical performance tester, wide-angle X-ray scattering (WAXS), small-angle X-ray scattering (SAXS), and thermogravimetric analysis (TGA). The results showed that the thermal stability of F-III fibers was enhanced to some extent, and the tensile strength and modulus of F-III fibers had great changes as the extension of treatment time during hot drawing in Sc-CO2, although the treatment temperature was lower than the glass transition temperature (Tg) of F-III fibers. Accordingly, the phase fraction, orientation factor fc of the (110) crystal plane, fibril length lf, and misorientation angle Bφ of all the samples were also investigated. Fortunately, the hot drawing in Sc-CO2 was successfully applied to the preparation of F-III fibers with high mechanical properties. [ABSTRACT FROM AUTHOR]

Efficient enhancement of the toughness of epoxy resins has been a bottleneck for expanding their suitability for advanced applications. Here, polysulfone (PSF) was adopted to toughen and modify the epoxy. The influences of PSF on the mechanical and thermal properties of the epoxy resin were systematically studied by optical microscopy, Fourier transform infrared spectrometer (FT-IR), differential scanning calorimetry (DSC), thermogravimetric analyzer (TG), dynamic mechanical thermal analyzer (DMA), mechanical tests and scanning electron microscope (SEM). The dissolution experimental results showed that PSF presents a good compatibility with the epoxy resin and could be well dissolved under controlled conditions. The introduction of PSF was found to promote the curing reaction of the epoxy resin without participating in the curing reaction and changing the curing mechanism as revealed by the FT-IR and DSC studies. The mechanical properties of PSF/epoxy resin blends showed that the fracture toughness and impact strength were significantly improved, which could be attributed to the bicontinuous phase structure of PSF/epoxy blends. Representative phase structures resulted from the reaction induced phase separation process were clearly observed in the PSF/epoxy blends during the curing process of epoxy resin, which presented dispersed particles, bicontinuous and phase inverted structures with the increase of the PSF content. Our work further confirmed that the thermal stability of the PSF/epoxy blends was slightly increased compared to that of the pure epoxy resin, mainly due to the good heat resistance of the PSF component. [ABSTRACT FROM AUTHOR]

The hot-drawing process of polyacrylonitrile (PAN) fibers is an important step during the production of PAN-based carbon fibers. In this study, supercritical carbon dioxide (Sc-CO2) was used as one kind of media for thermal stretching of PAN fibers to study the effect of different pressures of Sc-CO2 on crystallinity, degree of orientation and mechanical property of PAN fibers during the hot-drawing process. The changes of microstructure and mechanical properties in the PAN fibers were investigated by wide-angle X-ray diffraction, small angle X-ray scattering and monofilament strength analysis. The results showed that as the pressure increased, the crystallinity and degree of orientation of PAN fibers increased. Furthermore, when the pressure was 10 MPa, the crystallinity increased from 69.78% to 79.99%, which was the maximum crystallinity among the different pressures. However, when the pressure was further increased, the crystallinity and degree of orientation of the fibers were reduced. The test results of the mechanical properties were consistent with the trends of crystallinity and degree of orientation, showing that when the pressure was 10 MPa, the tensile strength of the fibers increased from 4.59 cN·dtex−1 to 7.06 cN·dtex−1 and the modulus increased from 101.54 cN·dtex−1 to 129.55 cN·dtex−1. [ABSTRACT FROM AUTHOR]

Thermal pre-oxidation of polyacrylonitrile (PAN) fibers is a time-consuming and energy-consuming step in the production of PAN-based carbon fibers. In this paper, the effect of temperature on the structures and properties of PAN fibers cyclized in the supercritical carbon dioxide (Sc-CO2) medium was studied. The thermal behaviors of the PAN fibers were investigated by Fourier transform infrared spectra (FT-IR), X-ray diffraction (XRD), differential scanning calorimeter (DSC) and thermogravimetric analysis (TGA). The cyclization reaction was sensitive to the heating temperature and gas atmosphere. The FT-IR results of the PAN fibers treated in the Sc-CO2 confirmed that the degree of cyclization increased with the increase of the cyclization temperature. Compared with the PAN fibers treated in the air, the PAN fibers treated in the Sc-CO2 showed a higher degree of cyclization even at the same temperature. These findings might be related to the osmotic action of Sc-CO2 causing the fibers to be further arranged in a regular manner, which was favorable for the cyclization reaction. Moreover, as one kind of high diffusion and high heat transfer media, the heat release during the cyclization of PAN fibers could be quickly removed by Sc-CO2, which achieved the progress of the rapid-entry cyclization reaction. [ABSTRACT FROM AUTHOR]

In this work, the layer-by-layer self-assembly technology was used to modify aramid fibers (AFs) to improve the interfacial adhesion to epoxy matrix. By virtue of the facile layer-by-layer self-assembly technique, poly(l-3,4-Dihydroxyphenylalanine) (l-PDOPA) was successfully coated on the surface of AFs, leading to the formation of AFs with controllable layers (nL-AF). Then, a hydroxyl functionalized silane coupling agent (KH550) was grafted on the surface of l-PDOPA coated AFs. The properties such as microstructure and surface morphology of AFs before and after modification were characterized by FTIR, XPS and FE-SEM. The results confirmed that l-PDOPA and KH550 were successfully introduced into the surface of AFs by electrostatic adsorption. The interfacial properties of AFs reinforced epoxy resin composites before and after coating were characterized by interfacial shear strength (IFSS), interlaminar shear strength (ILSS) and FE-SEM, and the results show that the interfacial adhesion properties of the modified fiber/epoxy resin composites were greatly improved. [ABSTRACT FROM AUTHOR]