Good quality contacts between metal and silicon emitter are crucial for high crystalline solar cell efficiencies. We investigate the impact of defects originating from electrically inactive phosphorus on contact formation within silver thick film metallized silicon solar cells. For this purpose, emitters with varying sheet resistance, depth, and dead layer were metallized with silver pastes from different generations. Macroscopic contact resistivity measurements were compared with the microscopic contact configurations studied by scanning electron microscopy. The density of direct contacts between Ag crystallites grown into Si and the Ag finger bulk is essential for low contact resistivity. The presence of glass-free regions needed for such direct contacts depends on the paste composition and on the surface texture, and does not vary with the Si emitter properties. Indeed, the decrease in contact resistivity correlates with increasing density of Ag crystallites embedded in the Si surface. Furthermore, the density of Si surface-embedded Ag crystallites scales proportional to the electrically inactive P and is independent of the sheet resistance. Using the newest silver paste, the Ag crystallite density is independent of the emitter doping, but the Ag crystallite size increases as a function of the thickness of the dead layer. Transmission electron microscopy characterization of the excess P-doped Si crystal lattice shows that significant strain and Si bond weakening may play a major role for both Ag crystallite nucleation and growth. Finally, we studied Si crystal defects by metallizing nanocracks, dislocations, and grain boundaries and found that Ag crystallite nucleation is defect-property dependent. Copyright © 2013 John Wiley & Sons, Ltd.

We have investigated the influence of diffusion temperature during phosphorus emitter diffusion from a spray-on source on the performance of screen-printed multicrystalline silicon solar cells. Because of the dual diffusion mechanism present at high concentration in-diffusion of phosphorus in silicon, applying lower diffusion temperatures for a longer duration results in significantly enhanced penetration of the low concentration tail relative to the high concentration region. Moreover, we show that the sheet resistance of in-diffused emitters from a high concentration source depends primarily on the extension of the high concentration region, thus significantly different emitter profiles can be manufactured without altering the sheet resistance considerably. Because of the enhanced tail penetration, emitters of a specified sheet resistance diffused at reduced temperatures can result in higher fill factors of screen-printed solar cells due to diminution of Schottky type shunts. Furthermore, emitters diffused at lower temperatures for longer durations can yield a higher gettering efficiency, resulting in increased bulk recombination lifetime, and thus a higher internal quantum efficiency at long wavelengths. The deeper tail extension of low temperature emitters, however, causes increased absorption within the highly recombinative emitter, resulting in current losses due to a lower internal quantum efficiency at short wavelengths. Copyright © 2006 John Wiley & Sons, Ltd.