Abstract: HfO2 and HfO2:Eu powders were synthesized with Pechini method at temperatures in the range of 600–1500°C. Structural, radioluminescence and photoluminescence properties of the powders were investigated. The highest light output of about 20% of the efficiency of commercial GOS:Eu was found for materials containing 0.5% of Eu and prepared at 1500°C. The data shows, that further improvement of light output could be obtained if materials are processed at yet higher temperatures. Emission spectra indicate that Eu3+ experiences variety of symmetries of its surroundings. Undoped materials produce broad band emission peaking at 480nm and showing a significant afterglow. [Copyright &y& Elsevier]

Nanocrystalline powders of Lu2O3:Eu with the activator content varying in the range of 0.2–10% were prepared through a combustion technique. The powders were only slightly agglomerated and the size of crystallites were about 30 nm. Some of the powders were co-doped with Mg, Ca, Sr, Ba, La of various concentrations. Such powders were cold-pressed and sintered at 1750°C for 5 h in vacuum. X-ray-excited luminescence spectra of both the powders and the sintered ceramics were recorded and the efficiency was compared to the commercial standard Gd2O2S:Pr,Ce,F X-ray phosphor. It was found that the nanocrystalline powders of Lu2O3:Eu,Ca emit photons four-times less than the commercial micron-sized Gd2O2S:Pr,Ce,F powder. In the case of sintered materials the emission efficiency from our Lu2O3:Eu5%, Ca was roughly equal to the efficiency of the commercial-sintered Gd2O2S:Pr,Ce,F. The co-doping ions were shown to have various effects on the transparency of the sintered Lu2O3:Eu. Mg hindered the sintering process producing completely opaque pellets. Other ions facilitated the sintering course and the best results were obtained by co-doping the samples with 0.5% of Ba. Sr and La also significantly stimulated the sintering and the final pellets were only slightly cloudy. [Copyright &y& Elsevier]

Abstract: La2Hf2O7 nanopowders doped with different Pr concentrations (0.05–10mol.%) were synthesized by the Pechini method. XRD measurements confirmed the single crystalline phase formed already at 800°C and the structure was cubic pyrochlore. Luminescence excitation and emission as well as radioluminescence spectra were recorded for the materials. Both optical and X-ray excitation of La2Hf2O7:Pr produced a red emission resulting from the 4f–4f transitions of Pr3+ ions. Luminescence of materials synthesized at low temperatures was characterized by broadband glass-type emissions, while heat treatment at 1400°C led to spectra showing the typical for crystalline hosts narrow and intense 4f–4f transitions of Pr3+. [Copyright &y& Elsevier]