An experimental investigation into the possibility of dose-rate effects and wall scatter in the thermoluminescent response of LiF:Mg,Ti (TLD-100) was carried out. The investigation was motivated by theoretical simulations predicting the possible presence of dose-rate effects coupled with the lack of detailed experimental studies. The dose rate was varied by changing the source to sample distance, by the use of attenuators, sources of 137Cs of various activities, filtration and the construction of identical geometrical irradiators of Teflon and stainless steel. Four levels of dose in the linear dose response region were studied at 10−2 Gy, 1.5 × 10−2 Gy, 0.1 Gy and 0.5 Gy to avoid complications in interpretation due to supralinearity above 1 Gy. At the dose of 1.5 × 10−2 Gy, the dose rate was varied by five orders of magnitude from 4.9 × 10−3 Gy s−1 to 4.9 × 10−8 Gy s−1. At the other levels of dose, a one to two orders of magnitude in dose rate was achieved. Within the measurement uncertainty of 5–10%, no dose-rate effects were observed in any of the experimental measurements and no changes in the shape of the glow curve were observed. The maximum wall scatter effect (Teflon to stainless steel) was measured at ~8% within the experimental uncertainty and well below expectations. The results are encouraging with respect to the accurate and reproducible use of LiF:Mg,Ti under various experimental conditions of irradiation. [ABSTRACT FROM AUTHOR]

The literature describing the experimental investigations of possible dose-rate effects in the thermoluminescence (TL) of LiF: Mg,Ti (Harshaw) is reviewed. The total lack of glow curve analysis, coupled with inclusion of all or part of the high temperature TL and absence of parallel measurements of possible dose-rate effects in the irradiation stage severely limit the scientific and technical level of the experiments. In addition, the experimental procedures are far from sufficient to warrant any conclusion concerning the presence or absence of dose-rate effects in the TL of LiF:Mg,Ti. This decision is contrary to the widely held belief that there are no dose-rate effects in the TL of LiF:Mg,Ti. In addition, the literature on dose-rate effects in the optical absorption (irradiation stage) of LiF is reviewed and is found contradictory. No dose-rate studies have been carried out on optical absorption in LiF:Mg,Ti. Kinetic simulations demonstrating the possibility, even likelihood, of dose-rate effects are also reviewed. Dose-rate effects are shown to be likely due to competition between excitation and recombination in the irradiation stage. Some other possible mechanisms involving multiple charge carrier trapping are suggested. Further definitive experiments are sorely needed, but the interested researcher should beware, it is not an easy task. [ABSTRACT FROM AUTHOR]