Search

Transient devices have attracted extensive interest because they allow changes in physical form and device function under the control of external stimuli or related commands and have very broad application prospects for information security, biomedical care and the environment. Transient bioelectrical devices were fabricated inspired by a silkworm moth breaking out of its cocoon, which has shown many advantages, including the use of mild stimulation, biocompatible materials, a simple process, and a universal strategy. For the fabrication of the transient devices, heat-sensitive microspheres with a 9.3 mol L−1 LiBr solution in wax shells were prepared by microfluidic technology, which were then assembled into silk fibroin (SF) electronic materials/devices, such as SF conductive film, an LED circuit on SF film, and a Ag/SF film/Pt/SF film memristor. The contribution from the LiBr/wax microspheres to the transient time of the SF films upon exposure to heat was quantitatively investigated. This approach was applied to transiently dissolve a flexible Ag-nanowire resistance circuit line on a SF substrate. Moreover, memristors constructed with a functional layer of SF were destroyed by melting the LiBr/wax microspheres. This technique paves the way for realizing transient bioelectrical devices inspired by biological behavior, which have been well optimized by nature via evolution.

A series of functional polyacetylenes bearing the fluorene moiety with different conjugated lengths and terminal substituents, poly[2-ethynyl-7-(4-nitrostyryl)-9,9-dioctyl-9H-fluorene] (P1), poly[2-ethynyl-7-(4-(4-nitrostyryl)styryl)-9,9-dioctyl-9H-fluorene] (P2), poly[2-ethynyl-7-(4-(4-methoxystyryl)styryl)-9,9-dioctyl-9H-fluorene] (P3), poly[2-ethynyl-7-(4-(4-methylstyryl)styryl)-9,9-dioctyl-9H-fluorene] (P4), and poly[2-ethynyl-7-(4-(4-methylstyryl)styryl)-9,9-didodecyl-9H-fluorene] (P5), were designed and prepared using [Rh(nbd)Cl]2 as the catalyst. Their structures and properties were characterized and evaluated by FTIR, NMR, UV, FL, GPC and TGA analyses. The optical limiting properties were investigated using 450 fs laser pulses at 780 nm. These results show that the incorporation of styryl/stilbene functionalized polyfluorenylacetylenes has endowed resultant polyacetylenes with novel near-infrared laser protection properties and enhanced thermal stability. The optical limiting mechanism for laser protection was studied. It was found that the optical limiting properties mainly originated from two-photon absorption (TPA) of molecules in the resulting polyacetylenes. Additionally, it was also found that the functionalized polyacetylene with a longer fluorene-based conjugated chromophore and a stronger terminal electron acceptor group exhibits better optical limiting properties because of the larger π-electron delocalization and dipolar effect.

Graphitic nitrogen-doped hierarchical porous carbon nanosheets for supercapacitor application were derived from an easily obtained and green silk by simultaneous ZnCl2 activation and FeCl3 graphitization at different heating temperatures. By increasing the heating temperature from 700 to 850 °C, the degree of graphitization and BET surface area rose to their highest levels, while the nitrogen doping content was maintained at 2.24 wt%. Carbonized silk at 850 °C displays a nanosheet morphology and a considerable specific surface area (1285.31 m2 g−1), and it was fabricated into a supercapacitor as an electrode material, exhibiting superior electrochemical performance with a high specific capacitance of 178 F g−1 at 0.5 A g−1 and an excellent rate capability (81% capacitance retention ratio even at 20 A g−1) in 1 mol L−1 H2SO4 electrolyte. A symmetric supercapacitor using carbonized silk at 850 °C as the electrodes has an excellent specific energy of 14.33 W h kg−1 at a power density of 251 W kg−1 operated over a wide voltage range of 2.0 V in aqueous neutral Na2SO4 electrolyte.

A series of modified waterborne polyurethanes were synthesized using a self-emulsifying method for high performance waterproof coatings, such as fluoride polyurethane (FPU), siloxane modified waterborne polyurethane (SPU) and the polyurethane containing fluorine and siloxane (FSPU). The structures of waterborne polyurethane were designed from scratch, and the contents of fluoride acrylic monomer (FMA) and siloxane contents (HO-PDMS) segments in FSPU were adjusted for high performance waterproof. It's found that the sample has lowest water absorption, higher water contact angles, and better mechanical/thermal properties, when the FMA content is 20 wt% and HO-PDMS content is 3 wt%. The mechanisms of improvement of contact angles were investigated, due to the vinyl group crosslinking, higher temperature can significantly improve the hydrophobicity of the films in emulsion polymerization and film forming process. Optimized FSPU has a promising future as a kind of waterborne waterproof coatings.