Nanocrystalline diamond (NCD) thin films grown by chemical vapour deposition have an intrinsic surface roughness, which hinders the development and performance of the films' various applications. Traditional methods of diamond polishing are not effective on NCD thin films. Films either shatter due to the combination of wafer bow and high mechanical pressures or produce uneven surfaces, which has led to the adaptation of the chemical mechanical polishing (CMP) technique for NCD films. This process is poorly understood and in need of optimisation. To compare the effect of slurry composition and pH upon polishing rates, a series of NCD thin films have been polished for three hours using a Logitech Ltd. Tribo CMP System in conjunction with a polyester/polyurethane polishing cloth and six different slurries. The reduction in surface roughness was measured hourly using an atomic force microscope. The final surface chemistry was examined using X-ray photoelectron spectroscopy and a scanning electron microscope. It was found that of all the various properties of the slurries, including pH and composition, the particle size was the determining factor for the polishing rate. The smaller particles polishing at a greater rate than the larger ones. [ABSTRACT FROM AUTHOR]

Chemical vapour deposition (CVD) grown boron-doped nanocrystalline diamond (B-NCD) is an attractive material for the fabrication of high frequency superconducting nanoelectromechanical systems (NEMS) due to its high Young's modulus. The as-grown films have a surface roughness that increases with film thickness due to the columnar growth mechanism. To reduce intrinsic losses in B-NCD NEMS it is crucial to correct for this surface roughness by polishing. In this paper, in contrast to conventional polishing, it is demonstrated that the root-mean-square (RMS) roughness of a 520 nm thick B-NCD film can be reduced by chemical mechanical polishing (CMP) from 44.0 nm to 1.5 nm in 14 hours without damaging the sample or introducing significant changes to the superconducting transition temperature, , thus enabling the use of B-NCD films in the fabrication of high quality superconducting NEMS. [ABSTRACT FROM AUTHOR]

Diamond is one of the hardest and most difficult to polish materials. In this paper, the polishing of {111} and {100} single crystal diamond surfaces by standard chemical mechanical polishing, as used in the silicon industry, is demonstrated. A Logitech Tribo Chemical Mechanical Polishing system with Logitech SF1 Syton and a polyurethane/polyester polishing pad was used. A reduction in roughness from 0.92 to 0.23 nm root mean square and 0.31 to 0.09 nm rms for {100} and {111} samples respectively was observed. [ABSTRACT FROM AUTHOR]