Search

Thermal energy storage (TES) systems are significant to solve inevitable intermittency and curtailment issues of clean renewable energy sources. Thus, the high-density and high-efficient TES technologies are required to achieve carbon neutrality. This study aims to synthesize an egg-carton-shaped paraffin microsheet for high-density latent heat storage. Poly(methyl methacrylate) (PMMA) microparticles (3 μm in diameter) are homogeneously placed onto a silicon wafer (10 × 10 mm2) via Langmuir–Blodgett technique. The PMMA monolayer on the silicon wafer is then dipped in a colloidal silica sol and dried to form the bottom structure of the egg-carton. Paraffin, a phase change material with a large melting enthalpy, is injected into the void space of the egg-carton produced by the decomposition of the PMMA particles. Finally, the upper silica shell covers the egg-carton structure with spherical paraffin to ultimately obtain an approximately 3.4-μm-thick microsheet for latent heat storage. The thermal performance of the paraffin microsheets is evaluated using differential scanning calorimetry. The encapsulation ratio, defined as the mass ratio of the paraffin to the microsheet, is calculated to be approximately 80.2%. This novel paraffin microsheet enables an increase in the TES capacity and ultimately overcomes poor heat transfer in paraffin owing to its low thermal conductivity. [Display omitted] • Egg-carton-shaped paraffin microsheet with 3.4 μm thickness is synthesized by Langmuir–Blodgett technique, sol-gel reaction, and dip-coating. • Low TEOS concentration improves denseness of the egg-carton-shaped SiO 2 structure. • 35% enhanced heat storage capacity was obtained in the paraffin microsheet, compared to water. [ABSTRACT FROM AUTHOR]

The issue of leakage in phase change materials (PCMs) severely restricts their use as thermal storage materials. In this study, waste coffee grounds-based biochar (WCG) was developed by carbonization and chemical modification as a support material for composite PCMs. The WCG/Paraffin wax (PW) composite PCMs were prepared using the melt impregnation method. The pore structure of alkali-modified biochar (OH-WCG) underwent significant development, and the surface area and total pore volume increased to 21.9 and 12 times that of unmodified biochar, respectively. Leak-free composite PCMs (OH-WCG-40) can be obtained when using OH-WCG as the support material at a biochar addition of 40 wt%. The characterization results indicated the physicochemical compatibility of the biochar in the composite PCMs with the PCMs. Differential scanning calorimetry (DSC) showed the phase transition temperature and the melting enthalpy of OH-WCG-40 were 46.28 °C and 97.69 J/g, respectively. The thermal conductivity of OH-WCG-40 was enhanced by 43% compared to pure PW. After 300 cycles, the composite PCMs exhibited nearly no change in mass and demonstrated good cycling stability. Therefore, alkali-modified biochar is a good support material for composite PCMs which can be used as a good thermoregulation material for temperature regulation of buildings and recycling of solar energy. [Display omitted] • The surface area of the NaOH-biochar is 21.9 times that of the untreated biochar. • The thermal conductivity of the composite PCM is 43% higher than that of paraffin. • The composite PCMs show no mass change after 300 cycles and had good stability. • Only 40 wt% of modified biochar is required to ensure no leakage of the paraffin. [ABSTRACT FROM AUTHOR]

The efficient use of solar energy can alleviate the energy shortage, so the photothermal conversion materials have been a hot spot for research. Improved thermal conductivity and higher enthalpy/flexibility can expand the practical application scenarios of photothermal conversion materials. Therefore, a flexible composite material for photothermal conversion is developed in this paper. Among them, carbon nanotube (MWCNT) is the photothermal conversion material, melamine foam (MF) is the supporting skeleton of the composite, and paraffin wax (PW) is the phase change material. According to the results, MWCNT/MF/PW has a high latent enthalpy of 240 J/g. The thermal conductivity of MWCNT/MF/PW (0.129 W/m·K) was improved by 95.5% compared to MF/PW (0.066 W/m·K). MWCNT/MF/PW have a high photo-thermal conversion efficiency (85.16%). Hence, MWCNT/MF/PW exhibit excellent shape recovery due to the response to light and heat. In addition, the outdoor light absorption experiment of the composite PCM water tank indicates that MWCNT/MF/PW as a shell wrapped water tank shows good light absorption and heat preservation effect, which is not available for general photothermal conversion materials. • The MWCNT, MF and PW composite phase change materials were prepared. • The light/heat shape recovery properties of CPCMs with MWCNT was investigated. • The light-absorbing property (85.16%) of composites was studied. • The insulating effect of MWCNT/MF/PW on tank temperature was investigated. [ABSTRACT FROM AUTHOR]

Traditional water-based PV/T systems have low heat storage density, high PV backsheet temperatures, and low energy utilization in practical applications. In this work, nanoparticles were applied to improve thermal conductivity and simultaneously emulsions were added to enhance energy storage density of the conventional heat transfer media. Furthermore, the synergistic effect of nanocomposite Phase Change Material Emulsions (PCME) as the heat transfer medium on the thermoelectric efficiency of PV/T was studied in a real system. Specifically, the water-based 30 % paraffin emulsions with graphene oxide (GO) concentration of 0.01, 0.02 and 0.03 wt% were prepared by ultrasonic stirring and their thermophysical properties were characterized. The results show that the 30 wt% paraffin emulsion with addition of 0.02 wt% GO has the phase change temperature of 35 °C, latent heat of 42.93 J/g, thermal conductivity of 0.505 W/(m·K) and viscosity coefficient of 0.91. It shows the thermal efficiency of the paraffin/GO emulsion increased by 92.28 %, the electrical efficiency increased by 8.87 %, the comprehensive efficiency increased by 45.75 %, and 15.8 % increase in heat collection for the heat exchange tank in comparison with the water. It is concluded application of PCME would improves the thermoelectric performance of the system than traditional water-based PV/T systems. • Applying paraffin emulsions with GO nanoparticles to a practical PV/T system. • Optimal nanocomposite paraffin emulsion is selected by performance testing. • Comparing the performance and pumping consumption with water-based PV/T systems. • Greater improvement in thermoelectric efficiency of PV/T systems compared to water. [ABSTRACT FROM AUTHOR]

Chemically activated biochar with richer pore structure and higher specific surface area is well suited for loading phase change materials (PCMs). However, the effect of structural characteristics and abundant surface functional groups of chemically activated biochar on the thermal properties of PCMs has not been systematically investigated. Here, shape-stable samples were prepared by introducing biochar obtained by activation with different chemical reagents (ZnCl 2 , H 3 PO 4 , KOH, and K 2 CO 3) into three organic PCMs (paraffin, stearic acid, and polyethylene glycol). The results indicated that the biochar activated by KOH possessed the highest specific surface area of 1344.45 m2/g, followed by biochar activated by ZnCl 2 , H 3 PO 4 , and K 2 CO 3 of 1297.35, 1062.74, and 891.38 m2/g, respectively. The loading capacity of KOH-activated biochar was as high as 82.12 %, 83.13 %, and 80.81 % for the three organic PCMs, and the melting enthalpies of corresponding composite PCMs were 163.82, 168.54, and 139.96 kJ/kg. Additionally, the influence degree on the enthalpies of the three PCMs was only 10.84 %, 12.26 %, and 7.74 %, while that of ZnCl 2 and H 3 PO 4 -activated biochar was as high as 53.61 % and 44.22 %, 52.10 %, and 57.74 %, 55.35 % and 45.79 % indicating the two biochar were not suitable as support materials for PCMs. Moreover, ZnCl 2 -activated biochar has the most apparent upgradation on PCMs' thermal conductivity, which could increase the thermal conductivity of the three organic PCMs by 1.318, 1.34, and 1.229 times, respectively, followed by H 3 PO 4 , K 2 CO 3 , and KOH-activated biochar. • Chemically activated biochar had larger specific surface area. • Encapsulation capacity of KOH-activated biochar for organic were significant. • Influence degree of ZnCl 2 and H 3 PO 4 -activated biochar was obvious. • ZnCl 2 -activated biochar had the most apparent upgradation on thermal conductivity. [ABSTRACT FROM AUTHOR]