Vanadium nitride was synthesized by the reaction of VCl4 and NaNH2 at room temperature. X-ray powder diffraction could be indexed as cubic VN with the lattice constant of a=4.134Å. Transmission electron microscopy image showed particle and hollow sphere morphology. The optical properties of the as-prepared VN were investigated. [Copyright &y& Elsevier]

Boron nitride hollow spheres were synthesized by the reaction of BBr3 and NaNH2 at room temperature; X-ray powder diffraction pattern could be indexed as hexagonal BN with the lattice constants of a=2.482 and c=6.701 A˚; high-resolution transmission electron microscopy image showed the hollow spheres consisted of BN nanoparticles, with diameter between 80 and 300 nm; a possible formation mechanism of BN hollow spheres was discussed. [Copyright &y& Elsevier]

Mn5Si3 nanocages and nanotubes were successfully synthesized by molten salt flux reaction at 650 °C. The samples were characterized with X-ray powder diffraction and transmission electron microscopy. The influence of the reactants molar ratio of MnCl2 to Mg2Si and reaction temperature on the phases and morphologies of the products were discussed. The possible mechanism of forming Mn5Si3 nanocages and nanotubes is discussed. [Copyright &y& Elsevier]

Abstract: Nanocrystalline neodymium disilicide was synthesized by co-reducing anhydrous neodymium trichloride and sodium fluorosilicate with metallic sodium in an autoclave at 650°C. The as-prepared product was characterized and studied by X-ray powder diffraction, transmission electron microscopy and thermogravimetric analysis. [Copyright &y& Elsevier]

B4C ultrafine powders were successfully synthesized at 450 °C through a new co-reduction route. The synthesis was carried out in an autoclave by using BBr3 and CCl4 as the reactants and metallic Na as the co-reductant. The X-ray powder diffraction pattern and Raman spectra indicate the formation of B4C. An atomic ratio of B to C of 4.09:1.0 was determined from X-ray photoelectron spectra. Transmission electron microscopy images shows that typical B4C crystallites are composed of uniform ultrafine spherical and rod-like particles. [Copyright &y& Elsevier]