The domain states and phase transitions in 0.67Pb(Mg1/3Nb2/3)O3–0.33PbTiO3 single crystals were investigated by studying their relative permittivity under various dc bias at constant heating and cooling rates. The orientation dependence of the bias field effect was revealed by examining the temperature dependence of relative permittivity as a function of crystal orientation (the 〈111〉, 〈011〉 and 〈001〉 directions) and dc bias field. The crystals basically have a macrodomain rhombohedral ferroelectric state in the ferroelectric phase under zero dc bias. External bias field could modulate the domain state and induce a stable macrodomain state in the crystals. Also, it is proposed that the dc bias applied along the 〈001〉 or 〈011〉 direction could induce a tetragonal ferroelectric phase or an orthorhombic ferroelectric phase, respectively, in an intermediate temperature range. [Copyright &y& Elsevier]

An optimum composition range (29%≤x≤31%) of 〈001〉 oriented (1−x)Pb(Mg1/3Nb2/3)O3–xPbTiO3(PMNT) crystals was ascertained for multilayer actuator applications, which exhibited high-strain and low-hysteresis behavior. A −1.5 kV/cm negative E-field can be applied to PMNT ferroelectric samples with low hysteresis. Forty layer actuators with individual element sizes of 7×7×0.7 mm3 were fabricated under identical processing conditions using two different materials: (1) single crystal PMNT and (2) commercial PZT-SF ceramics. Under free-load conditions, 48 μm displacements can been achieved in PMNT actuators at electric fields ranging from −1.5 to 10 kV/cm, which is more than twice the displacement of the PZT-SF actuators driven from −10 to 10 kV/cm. Under 4 kg loading, the displacements in PMNT stain actuators are decreased to 42.5 μm. [Copyright &y& Elsevier]

Electric-field-induced strain behavior of (1−x)Pb(Mg1/3Nb2/3)O3–xPbTiO3 (PMNT) crystals with different orientations and compositions was investigated for use as electromechanical actuators. Crystallographically, high strains with low hysteresis were achieved for 〈001〉 oriented rhombohedral crystals (29%≤x≤31%) near a morphotropic phase boundary, rather than 〈110〉 and 〈111〉. Domain instability could explain inferior strain levels and large hysteresis for 〈110〉 and 〈111〉 oriented crystals. Ultrahigh strain levels up to 1.8% could be achieved for 〈001〉 oriented PMNT crystals, being related to an E-field induced phase transition. −2 kV/cm negative E-field can be applied to PMNT ferroelectric material with low hysteresis. High strain with low hysteresis makes PMNT crystals promising candidates for high performance solid-state actuators. [Copyright &y& Elsevier]