Abstract: The effects of MoO3 concentration on the sintering and electrical properties of Ce0.8Nd0.2O1.9 + 500 ppm SiO2 (NDCSi) and (Ce0.8Nd0.2O1.9)1 − x (MoO3) x  + 500 ppm SiO2 ( x = 0.01, 0.02, 0.03, 0.04, 0.05, NDCSi + 1MoO3, NDCSi + 2MoO3, NDCSi + 3MoO3, NDCSi + 4MoO3, NDCSi + 5MoO3) prepared through a modified sol–gel method were systematically investigated. The structures and ionic conductivities were characterized by XRD, FE-SEM and EIS. The results indicated a sharp increase in densification and conductivity for the system of NDCSi containing small amount of MoO3. It shows that NDCSi + 3MoO3 exhibited much higher relative density (RD = 96%), higher conductivity (σ t = 1.25 × 10−2 S cm−1 at 600 °C) and lower activation energy (E a = 0.81 eV) compared with NDCSi and the other MoO3 doped-NDCSi samples. Furthermore, MoO3 could be used as an effective sintering aid and a grain boundary scavenger for NDCSi system. And we obtained the optimal amount of the MoO3 is 3 mol%. [Copyright &y& Elsevier]

Abstract: The effect of small addition of different sintering aids (MoO3 and WO3) on the electrical properties of Ce0.9Nd0.1O2−δ has been investigated. The (Ce0.9Nd0.1)1−x M x O2−δ (x = 0.0; M = Mo, W, x = 0.01; Ce0.9Nd0.1O2−δ : NDC, (Ce0.9Nd0.1)0.99Mo0.01O2−δ : NDCMo; (Ce0.9Nd0.1)0.99W0.01O2−δ : NDCW) solid solutions were prepared and characterized. The X-ray diffraction patterns indicate that all the samples are single phases with a cubic fluorite structure. Moreover, from the field-emission scanning electron microscopy results, it is found (Ce0.9Nd0.1)0.99M0.01O2−δ (M = Mo, W) sintered at 1300 °C for 15 h have better sinterability than Ce0.9Nd0.1O2−δ . The total conductivity by electrochemical impedance spectroscopy are ranked as: NDCW  > NDCMo  > NDC measured at 700 °C, which is attributed to microstructures. It can be concluded that MoO3 and WO3 are both effective and WO3 seems to be more potential as sintering aids on the optimization of electrical properties for ceria-based electrolytes. [Copyright &y& Elsevier]