Search

Abstract: The interdependence between plasma spray process parameters and porosity of YSZ coating microstructures was investigated with simultaneous consideration of the deposition efficiency. Based on a factorial experimental plan, the argon plasma gas flow, the current, the interaction of argon flow and current, and the spray distance for the Triplex II plasma gun were found to yield the main contributions to porosity as well as to deposition efficiency. Each of these three process parameters has a significant individual effect on the in-flight particle velocities and temperatures. The contribution to the effects on porosity arises almost exclusively from the particle temperature. Regarding the deposition efficiency, the larger contribution originates from the particle velocity. To achieve a targeted high porosity at reasonable deposition efficiency a simple linear regression model was applied yielding an argon flow of 50slpm and a current of 470A at a spray distance of 200mm as the optimum parameter set. The average particle temperature estimated for this optimum is just above the melting temperature. At this setting, a porosity of 17.7% and a deposition efficiency of 32.5% may be expected. At a greater spray distance and lower power density (lower current and/or higher argon plasma gas flow) the deposition efficiency was observed to drop considerably. The cooling of the particles here becomes critical, i.e. the particles are only partly molten. This was verified by an analysis of the density distributions of measured in-flight particle temperatures. [Copyright &y& Elsevier]

Abstract: Perovskite Ba(Mg1/3Ta2/3)O3, BMT has promising bulk properties (thermal conductivity ~2W/m-K and coefficient of thermal expansion ~11×10−6/K at 1473K) for thermal barrier coating (TBC) applications at high temperature. However, during atmospheric plasma spraying (APS), such material was found to lose constituents due to the differences of vapor pressures resulting to non-stoichiometric composition of deposited coatings. To investigate the extent of phase decomposition at spray distance and varying electric arc current, different feedstock powders were plasma sprayed into water and collected for chemical, microstructural and phase analyses. When the electric arc current was decreased from 500A to 300A, the decomposition of the powders was reduced and the microstructure of the deposited coatings was improved. The thermal cycling lifetime of the deposited coatings at ~1250°C surface temperature is also higher. [Copyright &y& Elsevier]

Abstract: Highly porous TiO2 coatings have been produced by suspension plasma spraying on ITO coated glass substrates. The deposition process could be optimized so that fine/nano grained highly porous coatings were obtained. Mean crystallite sizes well below 50 nm could be achieved in the coatings for the anatase phase. Special emphasis was on the establishment of a high volume fraction of the desired anatase phase. The best coatings showed values of about 90% of anatase phase. With these coatings photovoltaic cells could be produced. Different levels of layer thickness and porosity as well as contents of anatase phase have been investigated. In the paper details on the microstructure of the cells as well as the photovoltaic performance will be given. [Copyright &y& Elsevier]