Abstract: By performing Z-scan method with a femtosecond laser (800nm, 50fs, 1kHz), we investigated the third-order optical nonlinearities of a cuprous oxide (Cu2O) film. Single-phase Cu2O film deposited on a quartz substrate was obtained using the pulsed laser deposition technique. The structure properties, surface morphology and optical transmission spectrum were characterized by X-ray diffraction, scanning electron microscopy and double beam spectrophotometer, respectively. The Z-scan results show that the Cu2O film exhibits large nonlinear refractive index, n2 =3×10−3 cm2/GW, while the two-photon absorption coefficient, α 2 =40cm/GW, is relatively small. It implies that the Cu2O film is a promising candidate for nonlinear photonic devices. [Copyright &y& Elsevier]

Abstract: The Au/TiO2 composite films have been fabricated using the pulsed laser deposition technique. The optical transmission spectra of the films were investigated in the range from 300 to 900nm and the surface plasmon resonance peaks were observed varying from 550nm to 650nm. The optical nonlinearities of the as-deposited and annealed samples were investigated by the Z-scan method using a high-repetition-rate femtosecond laser. It was found that, for the as-deposited samples, the sign of nonlinear absorption coefficients (β) changed from negative to positive with increasing Au concentration. However, for all the annealed samples, the sign of β was found to be negative. The nonlinear responses induced by the cumulative thermal effects were suggested to contribute to this phenomenon. [Copyright &y& Elsevier]

Abstract: Titanium dioxide thin films have been synthesized on Si (100) substrates using pulsed laser deposition method (KrF: 248 nm, 20 ns, 5 Hz). The emission spectra of the plasma induced by ablating TiO2 target in the oxygen or argon ambient gas were analyzed. The influences of substrate temperature and ambient gas pressure on the structural properties of TiO2 films were discussed. The X-ray diffraction results show that the films deposited at 750 °C are (004)-oriented anatase phase and (110)-oriented rutile phase under the oxygen and argon pressure of 5 Pa, respectively. The scanning electron microscopy images indicate that the TiO2 films have a uniform and smooth surface and are composed of nanocrystal grains. The pure anatase and rutile phase TiO2 films are further proved by Raman spectromicroscopy. In addition, the optical transmission spectra and Fourier Transform infrared spectroscopy of the films were also studied. [Copyright &y& Elsevier]