In this study, transparent alumina and TiAl alloy were successfully brazed at 860°C-940 °C using Ag-21Cu-4.5Ti (wt%) filler metal. The microstructure and mechanical properties of the joints were investigated. SEM and TEM analysis showed the typical interfacial microstructure of the joints brazed at 900 °C for 5min was TiAl/β-Ti + AlCuTi/AlCu 2 Ti + AlCuTi/AlCu 2 Ti + Ag(s,s) + Cu(s,s)/(Cu,Al) 3 Ti 3 O/transparent alumina. The effects of brazing temperature and holding time on the microstructure and mechanical properties of TiAl/transparent alumina joint were studied. In addition, the effects of the dissolution and diffusion of TiAl on the microstructural evolution of the brazing seam were discussed. Shear strength analysis reveals that the shear strength of the joint increases at first and then decreases when brazing temperature rises. The maximum shear strength is 49 MPa when the joint is brazed at 900 °C for 5 min. [ABSTRACT FROM AUTHOR]

The multilayer Ti and Ni foils were designed to braze SiO 2 -BN diphase ceramic with Nb at 1140 °C for 5min. The interfacial microstructure was examined using scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), transmission electron microscope (TEM) and X-ray diffraction (XRD) methods, respectively. Experimental results and thermodynamical calculations showed that the interfacial microstructures between Nb and SiO 2 -BN ceramic were (βTi,Nb)-TiNi eutectic structure/TiNi + TiNi 3 /TiN + Ti 3 O 5 + TiB 2 + Ti 5 Si 3 . The effects of the Ti content in the Ti-Ni braze alloy on the microstructures of the joints were investigated. With the increase of the Ti content, less Ni 3 Nb formed in the joint and TiNi 3 phase successfully turned into TiNi and Ti 2 Ni. The effects of the Ti content in the Ti-Ni braze alloy on the shear strength of the joints showed that the optimum thickness of the TiN + Ti 3 O 5 + TiB 2 + Ti 5 Si 3 reaction area was about 13 μm and the maximum shear strength of 52 MPa was achieved when the Ti content was 45 wt.%. [ABSTRACT FROM AUTHOR]