Search

Abstract: Optimal surface nitriding is closely related to plasma chemical composition. The effects of Plasma-Immersion Ion Implantation (PIII) nitriding with 15% N2+85% H2 type mixtures have been studied. A simplified PIII facility was assembled around an evacuated Pyrex cylindrical 500 mm long reactor with a 190 mm inner diameter, over which a 3.2 mm wide antenna was coaxially wound with a 240 mm inner diameter. The system was supplied by a 13.56 MHz RF generator whose electric component developed the plasma discharge. After the admission of the gas mixture to the reactor vessel the breakdown took place within 5–15 Pa work pressure and 450–500W RF power. The main plasma parameters were characterized including a 1.8 × 1018 to 3.1 × 1018 m−3 density by means of double Langmuir probes. An additional DC power supply was selected in order to bias AISI 304 stainless steel samples with a view to improving the steel hardness properties without compromising its corrosion resistance. The samples treated at different temperatures and for several periods, were evaluated by means of X-ray diffraction (XRD), which indicated the formation of nitrides, identified as Fe3NiN and FeNiN and can be associated with the enhanced austenitic phase of the stainless steel. Scanning electron microscopy (SEM) assessed the atomic percentages of nitrogen both on the sample surface and through their cross-section. Vickers microhardness (HV) tests exhibited up to a 6–7 times increase at a 500g load. Finally, Raman spectroscopy studies established four active modes at 215, 267, 385 and 490 cm−1 with temperatures between 400 and 500 °C. [Copyright &y& Elsevier]

Abstract: We present some results obtained from nitriding of AISI 304 stainless steel substrates. The process take place in an inductively coupled plasma discharge supplied by a ∼300W source at 13.56MHz in a 85% hydrogen and 15% nitrogen gas mixture. The samples, placed into a pyrex glass discharge chamber (3.5cm diameter and 60cm long) were biased by DC power from 0 to −300V with respect to ground. The resulting hardness is a function of the increasing nitrogen concentration in the substrate and this, in turn, of the temperature which varied from 200 to 470°C. After nitriding at −300V, hardness values of 1790 HV under 10g loads and of 632 HV for 300g were measured. X-ray diffraction indicates that the expanded phase amplitude (γ N) depends on the substrate temperature. [Copyright &y& Elsevier]

Abstract: We present in this work some experimental results obtained from nitriding AISI 304 stainless steel at different temperatures by means of RF/DC generated 1015 m−3 density plasmas in the 1–4eV electron temperature range. The samples were biased up to −400V. Substrate temperatures have proved to be an influential factor in the diffusion of the ions impinging onto the material under treatment. In turn, the γ N shift expansion observed by XRD during this temperature increase is a function of the amount of nitrogen introduced to the sample and is related to the bias, the nitrided layer depth and the plasma characteristics. Thus, we have identified the substrate temperature as a global control variable in order to analyse the evolution of the nitrogen enrichment process through its influence on the X-ray diffraction imaging of the γ N shift in the samples. The optimization of the temperature is explored along with its limits in terms of the Cr precipitation threshold. [Copyright &y& Elsevier]