We have developed a new nanofilter using a carbon nanotube-silver composite material that is capable of efficiently removing waterborne viruses and bacteria. The nanofilter was subjected to plasma surface treatment to enhance its flow rate, which was improved by approximately 62%. Nanoscale pores were obtained by fabricating a carbon nanotube network and using nanoparticle fixation technology for the removal of viruses. The pore size of the nanofilter was approximately 38 nm and the measured flow rate ranged from 21.0 to 97.2 L/(min·m 2 ) under a pressure of 1–6 kgf/cm 2 when the amount of loaded carbon nanotube-silver composite was 1.0 mg/cm 2 . The nanofilter was tested against Polio-, Noro-, and Coxsackie viruses using a sensitive real-time polymerase chain reaction assay to detect the presence of viral particles within the outflow. No trace of viruses was found to flow through the nanofilter with carbon nanotube-silver composite loaded above 0.8 mg/cm 2 . Moreover, the surface of the filter has antibacterial properties to prevent bacterial clogging due to the presence of 20-nm silver nanoparticles, which were synthesized on the carbon nanotube surface. [ABSTRACT FROM AUTHOR]

Nickel-decorated multi-walled carbon nanotubes (Ni-MWCNTs) were synthesized using a colloidal method and an electroless plating method to form Ni nanoparticles on the surface of MWCNTs. The Ni electroless plating process was optimized with solutions at various pH (5, 6, 7, and 8) levels. The Ni-MWCNTs fabricated at pH 7 show the most stable Ni nanoparticles on the surface of the MWNCTs. After optimization of the Ni plating process, the Ni-MWCNTs/Sn-58Bi composite solder were fabricated with varying contents of (0, 0.05, 0.1 and 0.2 wt%) Ni-MWCNTs. The experimental results show that Ni-MWCNTs enhance the mechanical properties of Sn-58Bi solder. The shear strength of Sn-58Bi solder improves by about 14% with 0.1 wt% Ni-MWCNTs. Furthermore, the microstructure evolution after a high temperature storage test shows that Ni-MWCNTs have an effect on grain refining and interrupt growth of the Intermetallic compound layer. The distribution of Ni-MWCNTs could be recognized with the results of EPMA. [ABSTRACT FROM AUTHOR]