Inspired by the double-helix structure of biological DNA, low-volume fraction and high-strength Al 2 O 3 twisted honeycomb structures with characteristics similar to those of helical structures in the z -axis were prepared by digital light processing 3D printing technology. As the twist angle increased, the compressive strength of the fabricated Al 2 O 3 structure decreased, and the deformation mechanism of the Al 2 O 3 structures gradually changed from stretching-dominated to bending-dominated, which can be predicted by the Gibson–Ashby model. The relationship between the effective elastic modulus and the volume fraction that can be modified by varying the wall thickness was described by the Pabst–Gregorova exponential relationship. The compressive strength of the Al 2 O 3 structure with a twist angle of 0° can reach 62.4 MPa at a volume fraction of 13.3%, providing guidance to optimize lightweight structures of ceramics. [ABSTRACT FROM AUTHOR]

Herein, translucent alumina ceramics with fine complex geometric shapes are successfully fabricated by a digital light processing (DLP) process followed by vacuum sintering. The interlayer bonding condition is the key for preparing high‐quality translucent alumina for this layer‐by‐layer additive manufacturing (AM) method. The curing characteristics of alumina suspensions are carefully investigated by curing depth and polymerization conversion behavior. It is clear that the residual stress resulted from the polymerization process is more critical than the curing depth for selecting optimum curing time. Finally, high‐quality translucent alumina ceramic and complex structures are realized using this novel AM technique. It reveals that DLP 3D printing method can be a promising technology for the fabrication of transparent ceramics. [ABSTRACT FROM AUTHOR]

Solid Oxide Fuel Cells (SOFCs) are environmentally efficient energy conversion devices, but are partially limited by the complicated fabrication procedure. In this work, dense 8 mol% yttria-stabilized zirconia (8YSZ) ceramics were successfully realized through a DLP (digital light processing) stereolithography method and the electrolyte self-supported fuel cell was also tested at 800 °C. The sintering behavior of the as-printed planar samples were investigated and a fully dense ceramic can be achieved at 1450 °C. The total conductivity of the sintered 8YSZ can reach 2.18 × 10−2 S cm−1 at a test temperature of 800 °C, which is acceptable for practical application. For the electrolyte self-supported fuel cell test, a power density of 114.3 mW cm−2 can be achieved when Ni-8YSZ cermet and La 0.8 Sr 0.2 MnO 3 (LSM) were used as anode and cathode. It was demonstrated that 3D printing is a promising processing technique to build up electrolyte self-supported SOFCs with desired structure for the future development. [ABSTRACT FROM AUTHOR]