The growth, XRD patterns, spectral properties, and fluorescence decays of Yb:Ca 0.28 Ba 0.72 Nb 2 O 6 (Yb:CBN) with doping concentration of 1 at.% and 5 at.% were studied. The peak absorption cross-section and the emission cross-section were calculated. Larger Stark splitting of Yb:CBN offers the prospect of the quasi-four level laser operation. The fluorescence lifetimes are 0.64 and 0.73 ms for 1 at.% and 5 at.%, respectively. The FWHM of absorption and fluorescence spectra of 5 at.% Yb:CBN are 62 and 68 nm, which are broader than other ultrashort laser media. The results prove that Yb:CBN crystal is a good candidate as an ultrashort laser medium. [ABSTRACT FROM AUTHOR]

In this paper, we describe a thulium-doped (Lu,Y) 3 Al 5 O 12 mixed crystal that was designed and grown to achieve a large pulse energy in Q-switched laser operation. Its absorption cross-sections at 781.3 nm and 1629.2 nm were calculated to be 3.4 × 10 −21 cm 2 and 5 × 10 −21 cm 2 , respectively, and the emission cross-section at 2018.3 nm was calculated to be 1.92 × 10 −21 cm 2 . The highest single pulse energy of 1.4 mJ near 2.02 μm was realized in an actively Q-switched solid-state laser, and further power scaling was just limited by the damage of the crystal coating. Based on the calculated spectrum parameters, theoretical simulation of the single pulse energy that considering the cross-relaxation process was proposed, which was well consistent with the experimental results. [ABSTRACT FROM AUTHOR]