Search

Polyisocyanate and caprolactone were used to chemically functionalize nanocellulose (CNF). Composites of CNF, caprolactone-modified nanocellulose (CNF–CL) and polyisocyanate-modified nanocellulose (CNF–JQ)/MC nylon were fabricated by anionic ring-opening polymerization. The effects of the crystal structure, crystal morphology and crystallization process of MC nylon composites have been characterized by wide-angle X-ray diffraction (WAXD), polarized optical microscopy(POM) and differential scanning calorimetry (DSC). Isothermal crystallization kinetics were analyzed using the Avrami equation, and the crystallization rate, half-time, and Avrami exponent were calculated. The results show that the nucleation effects of CNF–JQ/MC nylon composites is increased with the CNF–JQ increase, and it is best compared with MC nylon, CNF/MC nylon and CNF–CL/MC nylon composites, so CNF–JQ can play the role of effective nucleating agent in MC nylon. We also discussed the non-isothermal crystallization of the composites. Analysis of the Jeziorny and Mo model demonstrates that the Zc values of CNF, CNF–CL, CNF–JQ/MC nylon composites increase, and the F(T) values decrease in order. This indicates that CNF–JQ can better promote the crystallization rate of non-isothermal crystallization of MC nylon. The results of this work demonstrate that CNF–JQ can be an effective nucleation agent and increase the crystallization rate of MC nylon compared with CNF–CL. The activation energy of the composites was studied using the kissing method, and the results showed that CNF–CL decreased the activation energy of MC nylon, and CNF and CNF–JQ increased the activation energy of MC nylon. [ABSTRACT FROM AUTHOR]

The copolyester poly(butylene glycol adipate-co-terephthalate/diphenylsilanediol adipate-co-terephthalate) (PBDAT) was synthesized by the melt polycondensation method using terephthalic acid, adipic acid, 1,4-butanediol, and diphenylsilylene glycol as the raw materials. The molecular chain structure, thermal properties, thermal stability, mechanical properties, and degradation behaviors of the copolyesters were investigated. The results showed that the prepared PBDAT copolyesters exhibited good thermal stability and mechanical properties. With the increase in diphenylsilanediol (DPSD) content, the thermal stability of PBDAT and the melting temperature both increased. The tensile strength and elastic modulus of PBDAT also exhibited an increasing tend. When the DPSD content was 12.5% (PBDAT-12.5), the tensile strength, the elastic modulus, and elongation at break were 30.56 MPa, 238 MPa, and 219%, respectively. With the increase in diphenylsilanediol content, the hydrophilicity of PBDAT decreased, but PBDAT still shows good degradability and the thermal degradation T5% temperature was 355 °C. The thermal degradation of PBDAT was also improved. [ABSTRACT FROM AUTHOR]

Inverted perovskite solar cells (PSCs) exhibit great potential for industrial application thanks to their low complexity and low fabrication temperature. Aiming at commercial applications, it is necessary to comprehensively consider the material consumption and its corresponding electrical performance. Here, a simple strategy has been proposed to obtain inverted PSCs with comprehensive performance, that is, reaching an acceptable electrical performance by reducing the usage of perovskite. More precisely, the inverted PSCs, whose perovskite film is prepared by 1.0 M precursor, yields a power conversion efficiency (PCE) of 15.50%, fulfilling the requirement for real commercial application. In addition, the thickness of the electron transport layer (C60 in this work) in the above inverted PSCs was further optimized by comparing the simulated absorption spectrum, J-V characteristics and impedance with three different thicknesses of C60 layer. More excitingly, the optimized device displays high storage stability which maintains more than 90% of its initial PCE for 28 days. Therefore, our work provides a simple and cost-effective method to reach good comprehensive performance of inverted PSCs for commercial applications. [ABSTRACT FROM AUTHOR]