Search

Abstract: Performance characteristics of a three electrolyte rechargeable acid–alkaline hybrid battery using a PbO2 positive plate and a nickel metal hydride (NiMH x ) negative electrode in separate electrolyte of H2SO4 and KOH were studied. This hybrid battery has three electrolytes in a single cell. A neutral K2SO4 salt solution was placed between the acid and alkaline compartments of the cell, in which a cation exchange membrane and an anion exchange membrane, were employed to separate these three electrolytes. The open circuit voltage of this hybrid cell was found to be 2.64V in an electrolyte configuration of 1M H2SO4|0.2MK2SO4|2M KOH electrolyte configuration, compared to 1.92V in the conventional lead-acid cell in 1M H2SO4 and 1.40V in a NiMH x cell in 2M KOH. This hybrid acid–alkaline PbO2/NiMH x battery was shown to operate with a voltage 20% higher than the conventional lead acid battery and 110% higher than nickel–metal hydride battery at 1/3C discharging rate. The concentrations of the three electrolytes, the dimension of the electrolyte chamber, and other cell/operation parameters with impacts on the hybrid cell performance were investigated. [Copyright &y& Elsevier]

Abstract: Vulcan XC-72R carbon supported Pd nanoparticles was obtained in a NH3-mediated polyol process without any protective agent and characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM) techniques. The added NH3 species is found to have a strong complex ability to Pd, which not only avoids the formation of Pd hydroxide precipitate resulted from Pd hydrolysis, but also restrains the further complete reduction of Pd. Temperature-programmed reduction equipped with a mass spectrometry (TPR-MS) is employed to study the reductive behavior of unreduced Pd complex in Pd/C catalyst and the results show that the post-treatment in a reductive atmosphere at higher temperature is needed to ensure the complete reduction of Pd. XRD patterns show the heat-treated Pd/C sample in a reductive atmosphere has a face centered cubic crystal structure and TEM image indicates that the dispersion of Pd nanoparticles on the carbon support is uniform and in a narrow particle size range. Thermodynamic data analysis is carried out to elucidate the possible reaction pathway for the preparation of Pd/C catalyst in this process. The obtained Pd/C catalyst shows high activity to formic acid oxidation and high selectivity to oxygen reduction reaction (ORR) with the presence of methanol. [Copyright &y& Elsevier]

Abstract: Well dispersed PtSn/C, PtRu/C and Pt/C electrocatalysts were synthesized by a modified polyol process and characterized by X-ray diffraction (XRD), transmission electron microscope (TEM) and inductively coupled plasma-atomic emission spectrometry techniques. XRD patterns show that Ru induces the contraction of Pt lattice parameter while Sn makes the Pt crystal lattice extended. Ethanol oxidation activities on the catalysts were studied via cyclic voltammetry (CV) and chronoamperometry (CA) methods at room temperature. It is found that the electrode potential plays an important role in the electrochemical behavior of ethanol oxidation on PtRu/C and PtSn/C catalysts. In the lower potential region, PtSn/C possesses higher performance for ethanol oxidation, while in the higher potential region PtRu/C is more active. The different promotion effects of PtSn/C and PtRu/C to ethanol oxidation can be explained by the structural effect and modified bi-functional mechanism in different potential region. Single cell test of a direct ethanol fuel cell (DEFC) was also carried out to elucidate the promotion effect of PtRu/C and PtSn/C catalysts on the ethanol oxidation at 90°C. [Copyright &y& Elsevier]

Pt–Fe/C catalysts were prepared by a modified polyol synthesis method in an ethylene glycol (EG) solution, and then were heat-treated under H2/Ar (10 vol.%) at moderate temperature (300 °C, Pt–Fe/C300) or high temperature (900 °C, Pt–Fe/C900). As comparison, Pt–Fe/C alloy catalyst was prepared by a two-step method (Pt–Fe/C900B). X-ray diffraction (XRD) and transmission electron microscopy (TEM) images show that particles size of the catalyst increases with the increase of treatment temperatures. Pt–Fe/C300 catalyst has a mean particle size of 2.8 nm (XRD), 3.6 nm (TEM) and some Pt–Fe alloy was partly formed in this sample. Pt–Fe/C900B catalyst has the biggest particle size of 6.2 nm (XRD) and the best Pt–Fe alloy form. Cyclicvoltammetry (CV) shows that Pt–Fe/C300 has larger electrochemical surface area than other Pt–Fe/C and the highest utilization ratio of 76% among these Pt-based catalysts. Rotating disk electrode (RDE) cathodic curves show that Pt–Fe/C300 has the highest oxygen reduction reaction (ORR) mass activity (MA) and specific activity (SA), as compared with Pt/C catalyst in 1.0 M HClO4. However, Pt–Fe/C catalyst does not appears to be a more active catalyst than Pt/C for ORR in 1.0 M HClO4 + 0.1 M CH3OH. Pt–Fe/C300 exhibits higher ORR activity and better performance than other Pt–Fe/C or Pt/C catalysts when employed for cathode in direct methanol single cell test, the enhancement of the cell performance is logically attributed to its higher ORR activity, which is probably attributed to more Pt0 species existing and Fe ion corrosion from the catalyst. [Copyright &y& Elsevier]

Abstract: Carbon supported PtSn alloy and PtSnO x particles with nominal Pt:Sn ratios of 3:1 were prepared by a modified polyol method. High resolution transmission electron microscopy (HRTEM) and X-ray microchemical analysis were used to characterize the composition, size, distribution, and morphology of PtSn particles. The particles are predominantly single nanocrystals with diameters in the order of 2.0–3.0nm. According to the XRD results, the lattice constant of Pt in the PtSn alloy is dilated due to Sn atoms penetrating into the Pt crystalline lattice. While for PtSnO x nanoparticles, the lattice constant of Pt only changed a little. HRTEM micrograph of PtSnO x clearly shows that the change of the spacing of Pt (111) plane is neglectable, meanwhile, SnO2 nanoparticles, characterized with the nominal 0.264nm spacing of SnO2 (101) plane, were found in the vicinity of Pt particles. In contrast, the HRTEM micrograph of PtSn alloy shows that the spacing of Pt (111) plane extends to 0.234nm from the original 0.226nm. High resolution energy dispersive X-ray spectroscopy (HR-EDS) analyses show that all investigated particles in the two PtSn catalysts represent uniform Pt/Sn compositions very close to the nominal one. Cyclic voltammograms (CV) in sulfuric acid show that the hydrogen ad/desorption was inhibited on the surface of PtSn alloy compared to that on the surface of the PtSnO x catalyst. PtSnO x catalyst showed higher catalytic activity for ethanol electro-oxidation than PtSn alloy from the results of chronoamperometry (CA) analysis and the performance of direct ethanol fuel cells (DEFCs). It is deduced that the unchanged lattice parameter of Pt in the PtSnO x catalyst is favorable to ethanol adsorption and meanwhile, tin oxide in the vicinity of Pt nanoparticles could offer oxygen species conveniently to remove the CO-like species of ethanolic residues to free Pt active sites. [Copyright &y& Elsevier]