Search

MXenes consisting of thin layers of transition metal carbides or nitrides are good candidates for electrode materials due to their excellent electrical conductivity and fast ion transfer. Electrospun carbon nanofibers are highly porous and electrically conductive, making them attractive for electrode materials. In this study, free-standing electrodes were prepared by the dip-coating of carbon nanofibers (CNFs) in the MXene (Ti3C2) colloidal solution, which was synthesized via the wet-etching of MAX (Ti3AlC2) phase, and their chemical structures were investigated by X-ray diffraction and Fourier transform infrared spectroscopy. In addition, scanning and transmission electron microscopy were used to investigate the morphological and crystallographic features of MXene-coated CNFs. Surface area and pore volumes were investigated by nitrogen adsorption/desorption measurements. Supercapacitor performance was studied by assembling a 3-electrode system with 1M aqueous sodium sulfate solution as an electrolyte. MXene-coated CNFs exhibited a maximum specific capacitance of 514 F/g at 0.5 A/g, with energy and power densities of 71.4 Wh/kg at 0.5 A/g and 2.3 kW/kg at 5 A/g, respectively, which are relevantly higher compared to the pristine CNFs due to the pseudocapacitive behavior of MXenes. They also showed comparable cyclic stability during 5000 cycles with the CNFs. This result indicates that MXene-coated carbon nanofibers can be effective electrode materials for electrochemical energy storage. [ABSTRACT FROM AUTHOR]

Nickel cobalt phosphide/carbon nanofibers (NiCoP/C) with an average diameter of approximate 200 nm are prepared by electrospinning combined with calcinations. Carbon nanofibers with an average pore size of 10.77 nm as conductive skeletons support the dispersed NiCoP nanoparticles with the size ranging from 20 to 80 nm, providing abundant reactive sites and facilitating the electrochemical reactions. The specific capacitance of NiCoP/C reaches 478 F g−1 at 2 A g−1 in a 3 M KOH electrolyte, showing superior electrochemical properties compared to its counterparts. After 5000 charge/discharge cycles at 10 A g−1, 99.99 % of initial specific capacitance is retained. In addition, an asymmetric supercapacitor assembled using NiCoP/C as positive electrode and activated carbon as negative electrode exhibits an energy density of 16.72 Wh kg−1 at a high-power density of 7250 W kg−1. Furthermore, the capacitance loss of the supercapacitor is only 0.04 % after 5000 cycles at 10 A g−1, which is mainly attributed to the enhanced stability of NiCoP nanoparticles owing to the assistance of carbon nanofibers as the skeleton. The synergistic effects of NiCoP nanoparticles and carbon nanofibers result in the boosted electrochemical performances. This study demonstrates the potential application of carbon nanofibers as conductive skeletons for nanostructured electrodes. • NiCoP/C nanofibers were prepared by electrospinning without the emission of PH 3. • Carbon nanofibers acted as skeletons and conductive channels for NiCoP. • Assembled NiCoP/C//AC supercapacitor achieved 16.72 Wh kg−1 at 7250 W kg−1. [ABSTRACT FROM AUTHOR]

Exploring energy storage devices and hydrogen evolution reaction electrode materials with high efficiency electrocatalytic activity, high energy density and low cost has broad prospects, but there are still huge challenges. Compared with traditional energy storage devices, supercapacitors (SCs) are a new type of energy storage device with broad development prospects. However, their practical application is significantly limited by the energy density of electrode materials. The practical application of hydrogen evolution reaction (HER) is limited by the high cost and scarcity of Pt-based precious metal catalysts. It is essential to develop materials with stable structure, low cost and abundant reserves. Here, in this paper, CoS 2 and CoSe 2 composites embedded in carbon nanofibers (CNFs) (expressed as CoS 2 -CoSe 2 /CNFs) were synthesized by electrospinning combined with in-situ growth Zeolite Imidazolate Framework-67 strategy, carbonization and subsequent selenium sulfide process. When employed as the positive material in supercapacitors, a specific capacitance of 292.2 F g−1 is achieved at a current density of 1 A g−1. The specific capacitance of asymmetric supercapacitors (ASCs) assembled with CoS 2 -CoSe 2 /CNFs-5 as positive materials remains stable with no significant change observed in specific capacitance even after undergoing 10,000 cycles. At the same time, when a current density of 10 mA cm−2 is applied in a 0.5 M H 2 SO 4 electrolyte solution, an overpotential reading of 189 mV is observed. The evidence mentioned above showcases the significant capacity of this substance for application in electrochemical energy storage and conversion. • The synergy of different components regulates the electronic structure. • The as-obtained materials exhibited a good energy storage and conversion performance. • The retention of the ZIF-67 skeleton structure can increases the number of active sites. [ABSTRACT FROM AUTHOR]

Using renewable biomass precursors to develop high-performance carbon electrodes is a promising approach for the advancement of supercapacitors. This work proposes a feasible strategy to prepare self-supporting flexible porous carbon nanofibers by electrospinning and carbonizing the mixture of cuttlefish ink, polyacrylonitrile (PAN) and polymethyl methacrylate (PMMA). The impacts of cuttlefish ink precursor on the structure, elemental composition, and capacitance properties of carbon nanofibers have been studied. Herein, the unique structural advantage of cuttlefish ink can significantly optimize the porous structure of carbon nanofibers. Due to the hierarchical porous structure, large specific surface area, hollow channels and high nitrogen content, the carbon nanofibers offer a high specific capacitance of 364.8 F g−1 at 0.5 A g−1 current density, alongside desirable rate performance and cycle life. Furthermore, the carbon nanofiber electrode performs good mechanical flexibility. The flexible solid-state supercapacitor based on this electrode exhibits 14.1 Wh kg−1 energy density at 0.4 kW kg−1 power density, and 97.8% capacitance retention after 5000 cycles. The favorable capacitive properties make this carbon nanofiber material a potential candidate for supercapacitor electrodes. [Display omitted] • Electrospun porous carbon nanofibers (CPP–CNF) were prepared from cuttlefish ink. • CPP-CNF features hierarchical pores and hollow channels. • CPP-CNF is mechanically flexible with superior capacitive performance. • The flexible supercapacitor achieves high energy density and cycling stability. [ABSTRACT FROM AUTHOR]

• MnO 2 /CNF/Ag nanofabric electrodes are developed for flexible supercapacitors. • The brittle issue in the CNF electrode is greatly improved by an Ag incorporation. • The optimized MnO 2 /CNF/Ag electrode has a specific capacitance of 184 F/g at 1 A/g. • An energy density of 16.3 Wh/kg and a power density of 400 W/kg was achieved. • A capacitance retention rate of 87 % was demonstrated when subjected to bending. Flexible supercapacitors are gaining increasing popularity due to their potential in powering portable, wearable, and lightweight electronic devices. In this study, we have successfully developed a high-performance flexible electrode for quasi-solid-state supercapacitors by incorporating Ag into carbon nanofibers (CNF) through electrospinning, and growing MnO 2 as an active material on the electrode using an in-situ redox method. The Ag and MnO 2 co-decorated CNF electrode offers several advantages over conventional CNF electrodes, including an enlarged reaction area, higher charge storage capacity, and improved resistance to brittleness issues. Among all the quasi-solid-state supercapacitors tested, the MnO 2 -decorated electrode with an optimized Ag incorporation exhibited the highest specific capacitance of 184 F/g at a current density of 1 A/g, representing a remarkable 17-fold increase compared to the reference CNF electrode. Furthermore, the Ag and MnO 2 co-decorated electrode demonstrated an energy density of 16.3 Wh/kg and a power density of 400 W/kg at the same current density. Notably, the electrode exhibited excellent flexibility, with a capacitance retention rate of 87 % when subjected to bending with a curvature ranging from 5 to 1.25 cm. Our results suggest that the Ag and MnO 2 co-decorated CNF electrode holds great promise for flexible energy storage applications. [Display omitted] [ABSTRACT FROM AUTHOR]