Samarium substituted 0.8Ba0.2(Bi0.5K0.5)TiO3 (here after abbreviated as BTBKT-20) lead free ceramics with composition 0.8Ba0.2(Bi0.5(1-x)Sm0.5xK0.5)TiO3 (where x=0.01,0.03,0.05) lead free ceramics have been prepared by solid state reaction and followed by high energy ball milling process. The present paper focuses the impedance and ac conductivity studies of Sm substituted BTBKT-20 lead free ceramics. Impedance spectroscopic studies revealthat temperature dependent relaxation process. Single depressed semi circle was observed in Cole-Cole plots, indicates non-Debye kind of relaxation process. Maximum grain resistance was observed for x=0.03 Sm substituted BTBKT-20 sample. Frequency and temperature dependent AC conductivity was calculated and it found to obey the universal Jonscher's power law and the values of activation energies suggest that conduction is ionic in nature. [ABSTRACT FROM AUTHOR]

0.8BaTiO3-0.2(Bi0.5(1-x)Nd0.5xK0.5)TiO3 (0.01 ≤ x ≤ 0.06) lead free ceramic materials have been prepared by solid state reaction method and followed by high energy ball milling process. X-ray diffraction studies confirm the tetragonal structure of the materials at room temperature. Lattice parameters and density are decreasing with increase of Nd substitution. Microstructure studies were done by using Scanning electron microscope and it found that grain size is decreasing with increase of Nd substitution. Temperature and frequency dependent dielectric studies reveal relaxor behaviour of the materials. Dielectric constant, dielectric loss and Curie temperature are decreasing with Nd substitution. Maximum Curie temperature of 195°C was observed at 1MHz for x=0.01 Nd substituted sample. Degree of diffuseness was calculated from the modified Curie-Weiss law and it is increasing with Nd substitution. AC conductivity is increasing with increase of Nd substitution and observed maximum activation energy of 0.52 eV for x=0.02 Nd substituted sample. [ABSTRACT FROM AUTHOR]