Search

The three-dimensional structure of oleic acid-capped CdSe and thiol-capped CdTe nanocrystals used as quantum dots has been determined by total synchrotron radiation x-ray diffraction and atomic pair distribution function analysis. Both CdSe and CdTe are found to exhibit the zinc-blende-type atomic ordering. It is only slightly distorted in CdSe implying the presence of nanosize domains and very heavily distorted in CdTe due to the presence of distinct core-shell regions. The results well demonstrate the great potential of the experimental approach and thus encourage its wider application in quantum dot research. [ABSTRACT FROM AUTHOR]

High-quality Er:ZnO films were grown by the pulsed-laser deposition technique at high temperature followed by in situ annealing. The films demonstrate remarkable crystalline quality and array of self-assembled grains. Although the films show very low electrical resistivity (∼6.41×10-4 Ω cm) at room temperature, a semiconductor-metal transition was observed at 190 K for low doping in contrast to semiconductor behavior for high doping. The films show pronounced room temperature emission at 1.54 μm, illustrating the activation of Er3+ ions in ZnO matrix. Furthermore, no quenching effects in 1.54 μm emission characteristics were observed up to 2 wt % of Er doping in ZnO at room temperature. [ABSTRACT FROM AUTHOR]

We report on the observation of remarkable room-temperature ferromagnetism in nanocrystalline epitaxial Co:TiO2 films grown on sapphire (0001) substrates by a pulsed-laser deposition technique using high-density targets. The films were characterized by x-ray measurements, atomic force microscopy, micro-Raman, electron-paramagnetic resonance, and magnetization studies. The films exhibit three-dimensional islandlike growth that contains nanocrystalline particles. Our experimental results suggest that the remarkable ferromagnetism in Co:TiO2 films is controlled either by the interstitial Co2+ ions or small clusters, which are mainly present at the interface and on the surface of the films. Our work clearly indicates that Co interstitials and nanoclusters cause room-temperature ferromagnetism in Co-doped TiO2. [ABSTRACT FROM AUTHOR]

We report the growth and magnetic characterizations of La0.7Ba0.3MnO3 and La0.7Sr0.3MnO3 films on SrTiO3-buffered Si (100) and Si (111) substrates by pulsed-laser deposition. The structural studies show the epitaxial nature of the films. The microscopic studies show that the films consist of nanocrystalline particles. All films display sharp magnetic and electrical transitions associated with the colossal magnetoresistance behavior at and above room temperature, illustrating the superior quality of the films. [ABSTRACT FROM AUTHOR]

We have demonstrated the fabrication of highly continuous and smooth CdSe semiconductor films containing self-assembled nanocrystals (NCs) using a simple, low cost solution-processed deposition technique. The impact of thermal annealing and ethanedithiol (EDT) treatment on oleate capped CdSe NCs films is illustrated. Post deposition EDT treatment enhances strong electron coupling between NCs by reducing the inter-particle distance, which enhances four orders of magnitude of photocurrent in the pn-device. Mild thermal annealing of NC films cause large redshift and significant broadening. Our findings suggest that NCs with short-range organic ligands are suitable for high-performance Thin-Film-Transistors and next generation high-efficiency photovoltaics. [ABSTRACT FROM AUTHOR]