The Sr1-xBaxTcO3 (x=0, 0.1, 0.2) oxides were prepared and their solid-state and magnetic structure studied as a function of temperature by x-ray and neutron powder diffraction. The refined Tc moments at room temperature and Néel temperatures for Ba0.1Sr0.9TcO3 and Ba0.2Sr0.8TcO3 were 2.32(14)μβ and 2.11(13)μβ and 714*C and 702*C, respectively. In contrast to expectations, the Néel temperature in the series Sr1-xAxTcO3 decreases with increasing Ba content. This observation is consistent with previous experimental measurements for the two series AMO3 (M=Ru, Mn; A=Ca, Sr, Ba) where the maximum magnetic ordering temperature was observed for A=Sr. Taken with these previous results the current work demonstrates the critical role of the A-site cation in the broadening of the π* bandwidth and ultimately the magnetic ordering temperature. [ABSTRACT FROM AUTHOR]

We present evidence for possibly the highest magnetic ordering temperature in any compound without 3d transition elements. Neutron powder diffraction measurements, at both time-of-flight and constant wavelength sources, were performed on two independently prepared SrTcO3 powders. SrTcO3 adopts a distorted perovskite structure with G-type antiferromagnetic ordering and has a moment of 1.87(4)μB per Tc cation at room temperature with an extraordinarily high Néel point close to 750 °C. Electronic structure calculations reveal extensive mixing between the technetium 4d states and oxygen states proximal to the Fermi level. This hybridization leads to a close relationship between magnetic ordering temperature and moment formation in SrTcO3.