Search

Surface etching of single-crystal diamond (SCD) in hydrogen plasma plays a decisive role for high-quality homoepitaxy and surface conduction of diamond. The complexity of surface/subsurface condition such as defects would give rise to the distinct morphology features and even further result in the unpredictable properties. Correspondingly, the evolutionary relationship between the morphology and electrical properties of mechanically polished SCDs which have typical cleavage damage in microns depth after hydrogen plasma treatment still needs to be further completed. In this work, the chemical vapor deposited (CVD) SCDs with uniform polishing-caused subsurface cleavage were immersed in microwave hydrogen plasma for variable duration. Time-dependent morphological evolution, multi-mode etched pits (EPs) (resulting from local defects/cracks and dislocations) and associated etching mechanism were comprehensively studied. At the early stage of plasma treatment before 60 min, owing to the obvious surface roughing generated by preferential etching (with the rate of >400 nm/h) of severe mechanically damaged regions, the hole mobility was significantly deteriorated, also accompanying with the apparent drop of sheet concentration. Concurrently, the deposited surface sp 2 amorphous carbon (a -C) nanodots on diamond surface and non- sp 3 hydrogen bonds reconstruction, which arising from defect-etching produced local abundant carbon-containing radicals or possible exfoliation generated by hydrogen penetration of massive defective regions, also would play an adverse role for the conduction associated with (100) C–H surface. However, the surface roughness was reduced from the maximum 13.2 nm–4.2 nm by prolonging etching, resulting from the smoothing effect of small-angle crystal misorientation on waved height difference related to the uniform (111) cleavage and the removal of dense irregular EPs associated with polishing-induced local defects as well as the vanishing of surface a -C nanodots. In this case, the improvement of surface electrical properties together with the negative correlation of the mobility and sheet concentration were appeared by the gradual formation of (100) diamond surface and the building of uniform (100) C–H bonds. • CVD SCDs with typical subsurface damages(defects) were treated in pure hydrogen plasma. • Morphology evolution associated with polishing defects was time-dependently presented. • Surface sp2 nanodots deposition from defect-etching and CH reconstruction would affect electrical properties. [ABSTRACT FROM AUTHOR]

In order to realize the practical use of diamond as a semiconductor material, large-area single-crystal diamond wafers with uniform quality are required. Mosaic growth is an effective method to produce inch-grade single-crystal diamonds. However, the quality of the wafer is limited by the junction interface seriously, because cracking occurs easily due to the high internal stress. In this paper, the repetition growth method was adopted to grow mosaic splicing single-crystal diamond without polycrystalline diamond interface. The high-quality single crystal diamond slices were reduplicated by microwave plasma chemical vapor deposition (MPCVD). The substrates were obtained by cutting a piece of CVD diamond along a plane perpendicular to 〈001〉 (with a (100)-oriented surface). The evolution of the growth characteristics around the junction of the substrates at different stages was studied. The results show that the surface of the epitaxial layers gradually evolves from blurry terraces to a regular well-ordered step flow. When the substrates have the same deviation direction and the off-direction angles are within 3°, the junction of the substrates can connect smoothly. Raman mapping shows that there is a mixture of tensile stress and compressive stress near the junction. As the thickness of the epitaxial layer increases from 280 μm to 560 μm, the range of tensile stress near the joint area expands from 85 μm to 150 μm, the maximum tensile stress increases from 0.08 GPa to 0.16 GPa. In addition, the value of FWHM in the X-ray rocking curve is less than 2.80 cm−1 around the junction, which indicates good crystal quality. [Display omitted] • The evolution of growth characteristics around the junction in the mosaic diamond was studied. • The mosaic boundary evolved from blurry terraces to a well-ordered step flow and finally connected. • The lowest value of tensile stress near the joint area was reported as the film thickness increased. • The larger FWHM of Raman peak around the junction is caused by the increased tensile stress. • The "inherit" effect of NV content of the epitaxial layer was observed for the corresponding substrate. [ABSTRACT FROM AUTHOR]