The slow reaction kinetics and structural instability of organic electrode materials limit the further performance improvement of aqueous zinc‐organic batteries. Herein, we have synthesized a Z‐folded hydroxyl polymer polytetrafluorohydroquinone (PTFHQ) with inert hydroxyl groups that could be partially oxidized to the active carbonyl groups through the in situ activation process and then undertake the storage/release of Zn2+. In the activated PTFHQ, the hydroxyl groups and S atoms enlarge the electronegativity region near the electrochemically active carbonyl groups, enhancing their electrochemical activity. Simultaneously, the residual hydroxyl groups could act as hydrophilic groups to enhance the electrolyte wettability while ensuring the stability of the polymer chain in the electrolyte. Also, the Z‐folded structure of PTFHQ plays an important role in reversible binding with Zn2+ and fast ion diffusion. All these benefits make the activated PTFHQ exhibit a high specific capacity of 215 mAh g−1 at 0.1 A g−1, over 3400 stable cycles with a capacity retention of 92 %, and an outstanding rate capability of 196 mAh g−1 at 20 A g−1. [ABSTRACT FROM AUTHOR]

Recently, aqueous zinc‐based batteries (AZBs) have become a promising candidate for energy storage devices due to the high safety of aqueous electrolytes and the appealing features of Zn anodes, for example, low cost and high theoretical capacity. However, the excessive growth of Zn electrodeposits as well as the uneven stacking of large hexagonal Zn crystal units always render loose and irregular electrodeposition or even dendritic growth, which seriously deteriorates the actual performance of AZBs. Herein, to refine the grain size of Zn electrodeposits, a trace of Pb2+ ions as a novel electrolyte additive is performed to inhibit the growth of Zn grain during the Zn electrodeposition. Owing to the higher adsorption energy of Pb2+ ions on Zn crystal when compared with Zn2+ ions, the strongly positively‐charged Pb2+ ions are tightly absorbed on the typical crystal planes of initially‐formed Zn nuclei, which block the way for the subsequent absorption and electroreduction of Zn2+ ions. As a result, the Pb2+ ions‐containing electrolyte refines the grain size of Zn electrodeposits from 7.43–7.87 μm to 0.88–2.26 μm, and affords a high reversibility of Zn plating/stripping behavior with a high Coulombic efficiency of 99.9 % over 1000 cycles. [ABSTRACT FROM AUTHOR]