Search

In the practical operation of an electromagnetic pulse (EMP) simulator, the flashover phenomenon on the edge of polypropylene dielectrics dominates the insulation failure mode of a peaking capacitor. To analyze the characteristics of polypropylene film flashover voltage under high-pressure SF6, an experimental platform was established, and the pulse generator could output a pulse with a rise time of approximately 27 ns. The experiments were performed on finger electrodes, and the SF6 pressure was set from 0.1 to 1.0 MPa. The experimental results show that the relationship of flashover voltage and gas pressure could be divided into two regions: in low-pressure regions, the flashover voltage increases with the gas pressure linearly and in high-pressure regions, the growth of flashover voltage gradually slows down and approaches a saturation value. As the gap distance increases, the saturation point of gas pressure decreases, and even when close to 0.4 MPa, with a 9-mm gap distance, this unconventional phenomenon cannot be ignored, particularly in practical EMP simulators. When the high surface resistivity and the charge trap distribution on the polypropylene film are considered, the accumulation and emission of surface charges on the film might be the primary reason for the saturated phenomena. [ABSTRACT FROM AUTHOR]

The polymer film dielectric has been widely used in high voltage equipment for bulk insulation owing to the excellent insulation performance. Martin’s empirical formula for bulk breakdown is frequently used to predict the breakdown field strength of multilayer thin film with different electrode areas. In this article, based on the academic consensus that the cumulative breakdown probability of single-layer film obeys the Weibull distribution, the relationship between the cumulative breakdown probability of film dielectric under different electrode areas and the applied electrical field is deduced. Moreover, the relationship between the cumulative breakdown probability of film dielectric with various numbers of film layers and the applied electrical field is obtained and simplified. On these bases, combined with the experimental results of the average breakdown field of film dielectric with smaller electrode areas and fewer layers, a prediction model of the average breakdown field strength of film dielectric with different electrode areas and film layers is established. To obtain the solution of the prediction model concerning the number of film layer, an effective approximate solution method is proposed to solve the calculation problem with ultralarge and ultrasmall data, which significantly reduces the complexity of the solution process. A coaxial film capacitor is developed and tested to verify the prediction model with the “Chenguang” accelerator. The experimental breakdown field strength of 54 layers of 15 $\mu \text{m}$ biaxially oriented polypropylene (BOPP) film with an electrode area of 218.1 cm2 is 355.6 V/ $\mu \text{m}$ , which is comparable to the predicted result of 374 V/ $\mu \text{m}$. The prediction model presented in this article is of certain reference significance for the insulation design of film dielectrics. [ABSTRACT FROM AUTHOR]

Due to its low-loss and high dielectric strength, polypropylene is widely used as electrical insulation material in pulse capacitors. In order to study its breakdown characteristics for nanosecond voltage pulses, an experimental setup was designed to generate voltage pulses with a 10%–90% rise time of 38 ns and a full width at half maximum of about 90 ns. Tests of the three polypropylene films with thicknesses of 12, 15, and $18~\mu \text{m}$ were performed. In addition, hundreds of nanoseconds pulse and dc voltage were also applied for comparison. The experimental results reveal that most of the breakdown occurs during the front edge of the pulse for tens of nanoseconds pulse, and the breakdown strengths of the three kinds of polypropylene films are almost identical for different applied voltages, which show a weak correlation between the thickness of the dielectric and the breakdown field. The expected breakdown strength of tens of nanoseconds pulse defined in this paper is not significantly higher than the mean value of the hundreds of nanoseconds pulse and the dc condition, suggesting that the breakdown of a thin polypropylene film is mainly determined by the electrical field but not the voltage-time cumulative effect. All these observations strengthen the conclusion that the breakdown of a thin polypropylene film is an intrinsic phenomenon. [ABSTRACT FROM AUTHOR]