With the development of laser technology, laser-related materials have been widely studied. Both laser stealth coatings and laser protective coatings are currently the focus of attention. However, less research has been done on laser stealth and protective integrated coatings. In this paper, plasma-sprayed Y 2 O 3 –Ti 3 AlC 2 coatings were prepared with low-power (LP) and high-power (HP) parameters, and their laser stealth and laser protection properties were characterized. The LP coating and HP coating appeared to have lower reflectivity at 1064 nm because a low-reflectivity second phase and many loose flocs on the surface are introduced, which indicates excellent laser stealth performance. When irradiated by a laser, the LP coating exhibited excellent laser protection ability, and its reflectivity increased after irradiation because Ti 3 AlC 2 oxidized and decomposed and densely arranged small particles formed on the surface. The LP coating perfectly protected the 500-W laser irradiation for 20 s. In addition, the laser damage threshold of the LP coating was 5.599 s at 1000-W laser irradiation, which indicates that the LP Y 2 O 3 –Ti 3 AlC 2 coating is a potential material with laser stealth and laser protection integration. [ABSTRACT FROM AUTHOR]

High-energy lasers can cause severe damage to conventional materials in an extremely short time. Highly reflective coatings are effective against damage, but they cannot withstand high laser power densities. In this study, a composite coating with two characteristics, namely, reflection and energy consumption, was designed and prepared. TiO 2 and BN powders, as light reflective media, were introduced into a boron-modified phenolic resin (BPF) to prepare an anti-laser composite coating. The results show that the initial reflectivity of the composite coating can reach 78.8% at a wavelength of 1064 nm. After damage-free protection for 0.4 s, ablation occurred in the irradiation region. Owing to the formation of residual char, which is the pyrolysis product of BPF, the coating maintained its protective performance. When the composite coating was irradiated at 1000 W/cm2 for 10 s, the back-surface temperature was 186 °C, which indicates decent anti-laser performance. We also studied the role of BN by setting a control experiment. The high conductivity and energy consumption caused by the evaporation of B 2 O 3 , which is the oxidation product of BN, helped in improving the anti-laser performance. The residual char with high porosity and degree of graphitization proved to be effective to isolate laser energy. This study provides a new design for protection of conventional materials against laser damage. [ABSTRACT FROM AUTHOR]