Abstract: Yb3+-doped (Lu0.5Y0.5)3Al5O12 (Yb:LuYAG) single crystal has been grown by the Czochralski method. The segregation coefficient of Yb3+ was studied by the inductively coupled plasma atomic emission spectrometry (ICP-AES) method. The crystal structure has been determined by X-ray diffraction analysis. The absorption and emission spectra and fluorescence lifetime of Yb:LuYAG crystal were measured at room temperature. The spectroscopic parameters of Yb:LuYAG crystal were compared with those of Yb:YAG and Yb:LuAG crystals with the same doping level. The results indicate that Yb:LuYAG crystals are potential candidates for high-power ultrashort pulse lasers. [ABSTRACT FROM AUTHOR]

Abstract: A Yb3+-doped CaYAlO4 laser crystal has been grown by the Czochralski technique. The segregation coefficient was measured by Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES). The cell parameters were analyzed with X-ray diffraction experiments. Color defects in Yb:CaYAlO4 have been evidenced to be similar to those in undoped CaYAlO4. The polarized absorption spectra and the fluorescence spectrum of the Yb:CaYAlO4 crystal were measured at room temperature. The fluorescence decay time of the Yb3+ ion was investigated. The results show that Yb:CaYAlO4 has potential as a laser gain medium for an ultrashort laser system. [Copyright &y& Elsevier]

Yb3xY3(1−x)Al5O12 crystals with different Yb3+ concentration have been grown by the Czochralski method. The distribution coefficient of Yb3+ is 1.08±0.01, and it has little relation with Yb3+ concentration. The lattice parameter of YbAG is 1.193799±0.000054 nm. We have found an equation connecting the lattice parameter and Yb3+ concentration: α(x)=1.200976−0.007072x nm. [Copyright &y& Elsevier]

Abstract: A high optical quality erbium doped Lu2SiO5 single crystal has been grown by the Czochralski method. The distribution coefficient of Er3+ was measured to be ∼0.926. The absorption and emission spectra as well as the fluorescence decay curve of the excited state 4I13/2 were measured at room temperature. The spectroscopic parameters were calculated using the Judd–Ofelt theory, and the J–O parameters Ω 2 , Ω 4 and Ω 6 were found to be 4.451×10-20, 1.614×10-20 and 1.158×10-20 cm2, respectively. The room-temperature fluorescence lifetime of the Er3+ 4I13/2→4I15/2 transition was measured to be 7.74ms. The absorption and emission cross-section as well as the gain cross-section in the eye-safe regime of 1400–1700nm were also determined and discussed. [Copyright &y& Elsevier]