Search

Ferromanganese nodules represent an industrially untapped source of valuable metals (Mn, Cu, Ni, Ti, Co) but are still just the object of scientific research. In comparison with already utilized rocks, deep-sea deposits are too hard to reach for their full-scale mining to be profitable. Despite of this, current marine engineering allows us to conduct complete exploration and obtain mineral samples. We can already now develop low-cost methods for subsequent processing in anticipation of improved and safer future mining technology. But in what form would be the final product the most applicable? In our study, we reduced the pyro metallurgical pretreatment of raw nodules to two simple steps: roasting and aluminothermic reduction. Then we added a product, manganese-based alloy, to pure aluminum as a new alloying additive. As a reference for experimental alloys, commercial cast AlMn10 master alloy was chosen. The tested samples were prepared using two advanced operations of powder metallurgy: melt-spinning and spark plasma sintering (SPS). Microstructure was described in detail, tribological and selected mechanical properties were measured, and a comparative analysis was conducted. New additive gradually improved properties of alloys to a level close to 3xxx industrial alloys with its increasing percentage in pure aluminum. Measured values did not surpass the referent AlMn10, but there was not recorded any adverse impact associated with the origin of alloying mixture. • New aluminum alloys with the natural additive – reduced deep-sea nodules – modified by rapid solidification. • Extremely fine-grained microstructure with the content of supersaturated matrix regions. • Improved mechanical and tribological properties comparable to commercial alloys of 3xxx group. • Uncommonly high plasticity. [ABSTRACT FROM AUTHOR]

Due to the lack of mineral resources, unconventional raw materials have to be considered. In this work, the use of reduced deep-sea nodules from Clarion-Clippertion Fracture Zone of Pacific Ocean was tested as the natural mixture of alloying elements for aluminum alloys. The nodules were reduced by aluminothermic process without the extraction of individual elements. As the technology for the manufacture of the alloys, the powder metallurgy comprising mechanical alloying and spark plasma sintering was applied. The produced Al-Mn based alloys are characterized by uncommon spherical morphology of Al-Mn intermetallics, which leads to a significant ductility even in the case of high total amount of additives (up to 20 wt%). The wear resistance of the alloys strongly increases with growing amount of the reduced deep-sea nodules. • New aluminum alloys with reduced deep-sea nodules prepared by powder metallurgy. • Unique rounded morphology of intermetallics was obtained. • Improved strength compared with common Al-Mn alloys. • Reduced deep sea nodules improve tribological properties of aluminum. [ABSTRACT FROM AUTHOR]

An innovative way to utilize deep-sea manganese nodules is described in this paper. The manganese nodules were reduced by aluminothermy and subsequently added into aluminum as a mixture of alloying elements in their natural ratio. The microstructure and properties of aluminum alloys containing 1.2, 7.7, and 9.7 wt % of reduced nodules were studied. The alloys were formed by Al matrix and minor amounts of Al6(Fe,Mn) and Al11Fe7 intermetallic phases. The alloys containing a higher amount of reduced nodules are characterized by very good thermal stability. The obtained alloys were studied by X-ray diffraction, their microstructure was observed by scanning electron microscopy, and their local chemical composition was analyzed by energy dispersive spectrometer. The hardness of the samples was measured on the initial materials and after long-term annealing. Based on the obtained results, the aluminum alloys, with the addition of reduced deep-sea nodules, can serve as precursors for processing, e.g., by rapid solidification or hot working methods. [ABSTRACT FROM AUTHOR]