Abstract: This work is devoted to the preparation of ultrafine material based on Al–Cu–Fe quasicrystalline phase by powder metallurgy using mechanical alloying and Spark Plasma Sintering. The dependence of microstructure and phase composition of powders on the conditions of mechanical alloying was described. It was found that the Al60Cu30Fe10 quasicrystalline phase forms directly already after 2 h of milling under optimized conditions. The stability of this quasicrystalline phase was studied at various temperatures of Spark Plasma Sintering compaction process. [Copyright &y& Elsevier]

Abstract: In this work, Ti–Al–Si alloys were prepared by reactive sintering. The contents of silicon and aluminium ranged between 0–30wt.% and 0–36wt.%, respectively. Powders of titanium, aluminum, silicon and AlSi30 master alloy prepared by mechanical machining and/or milling were used for sintering. Powders were blended and pressed at room temperature. Sintering was carried out at 900°C for 30min. It was found that it is possible to produce compact materials with the structure corresponding to the as-cast materials when silicon is in the range of 15–20wt.% and aluminium content between 8 and 30wt.%. It was shown that these materials contain two phases—Ti5Si3 and TiAl. The central porosity can be reduced by induction heating. [Copyright &y& Elsevier]

Composite material prepared by spark plasma sintering (SPS) from a powder mixture of AlCrFeSi rapidly solidified alloy and 5 wt. % of Ni particles was studied in this work. It was proven that during SPS compaction at 500 °C, no intermetallic phases formed on the surface of Ni particles. The material exhibited sufficient mechanical properties obtained by tensile testing (ultimate tensile stress of 203 ± 4 MPa, ductility of 0.8% and 0.2% offset yield strength of 156 ± 2 MPa). Tensile samples were pre-stressed to 180 MPa and annealed at 450 and 550 °C for 1 h. Annealing at 450 °C did not lead to any recovery of the material. Annealing at 550 °C caused the full recovery of 0.2% offset yield strength, while the ductility was decreased. The self-healing behaviour originates from the growth of intermetallic phases between the Ni particle and the Al matrix. The sequence of NiAl, Ni2Al3 and NiAl3 intermetallic phases formation was observed. In particular, the morphology of the NiAl3 phase, growing in thin dendrites into the Al matrix, is suitable for the closing of cracks, which pass through the material. [ABSTRACT FROM AUTHOR]

Abstract: Rapidly solidified aluminum alloys are promising materials with very fine microstructure. The microscopy observation of these materials is complicated due to overlay of fcc-Al matrix and different intermetallic phases. A possible way to solve this problem is to dissolve the Al matrix. By this process powder formed by single intermetallic phase particles is obtained. In this paper a new aqueous based dissolving agent for Al-based alloy is presented. The influence of oxidation agent (FeCl3) concentration on quality of extraction process was studied. [Copyright &y& Elsevier]