Search

Due to the lack of mineral resources, unconventional raw materials have to be considered. In this work, the use of reduced deep-sea nodules from Clarion-Clippertion Fracture Zone of Pacific Ocean was tested as the natural mixture of alloying elements for aluminum alloys. The nodules were reduced by aluminothermic process without the extraction of individual elements. As the technology for the manufacture of the alloys, the powder metallurgy comprising mechanical alloying and spark plasma sintering was applied. The produced Al-Mn based alloys are characterized by uncommon spherical morphology of Al-Mn intermetallics, which leads to a significant ductility even in the case of high total amount of additives (up to 20 wt%). The wear resistance of the alloys strongly increases with growing amount of the reduced deep-sea nodules. • New aluminum alloys with reduced deep-sea nodules prepared by powder metallurgy. • Unique rounded morphology of intermetallics was obtained. • Improved strength compared with common Al-Mn alloys. • Reduced deep sea nodules improve tribological properties of aluminum. [ABSTRACT FROM AUTHOR]

One of the current problems concerning the re-use of aluminium alloys is the recycling of aluminium alloys with increased content of iron. One of the recent trends is the processing by powder metallurgy, producing completely new grades of aluminium alloys. The aim of the present work was to test the properties of Al–Si–Fe alloy, which can be manufactured from the high-irony scrap, as a possible material for elevated temperature applications. Since chromium and nickel accompany the iron in the scrap when stainless steels are admixed, the effect of chromium and nickel on thermal stability and mechanical properties at room and elevated temperature was also studied. Al–Si–Fe–X alloys were rapidly solidified by using melt spinning technique. The rapidly solidified ribbons were pulverized by planetary ball mill and the obtained powders were used for compaction by means of Spark Plasma Sintering. It was found that nickel improves the thermal stability as well as the mechanical properties at the elevated temperature. On the other hand, the effect of chromium on the mechanical properties at elevated temperature was almost detrimental. [ABSTRACT FROM AUTHOR]

Abstract: This work is devoted to the preparation of ultrafine material based on Al–Cu–Fe quasicrystalline phase by powder metallurgy using mechanical alloying and Spark Plasma Sintering. The dependence of microstructure and phase composition of powders on the conditions of mechanical alloying was described. It was found that the Al60Cu30Fe10 quasicrystalline phase forms directly already after 2 h of milling under optimized conditions. The stability of this quasicrystalline phase was studied at various temperatures of Spark Plasma Sintering compaction process. [Copyright &y& Elsevier]

Abstract: In this work, Ti–Al–Si alloys were prepared by reactive sintering. The contents of silicon and aluminium ranged between 0–30wt.% and 0–36wt.%, respectively. Powders of titanium, aluminum, silicon and AlSi30 master alloy prepared by mechanical machining and/or milling were used for sintering. Powders were blended and pressed at room temperature. Sintering was carried out at 900°C for 30min. It was found that it is possible to produce compact materials with the structure corresponding to the as-cast materials when silicon is in the range of 15–20wt.% and aluminium content between 8 and 30wt.%. It was shown that these materials contain two phases—Ti5Si3 and TiAl. The central porosity can be reduced by induction heating. [Copyright &y& Elsevier]

Composite material prepared by spark plasma sintering (SPS) from a powder mixture of AlCrFeSi rapidly solidified alloy and 5 wt. % of Ni particles was studied in this work. It was proven that during SPS compaction at 500 °C, no intermetallic phases formed on the surface of Ni particles. The material exhibited sufficient mechanical properties obtained by tensile testing (ultimate tensile stress of 203 ± 4 MPa, ductility of 0.8% and 0.2% offset yield strength of 156 ± 2 MPa). Tensile samples were pre-stressed to 180 MPa and annealed at 450 and 550 °C for 1 h. Annealing at 450 °C did not lead to any recovery of the material. Annealing at 550 °C caused the full recovery of 0.2% offset yield strength, while the ductility was decreased. The self-healing behaviour originates from the growth of intermetallic phases between the Ni particle and the Al matrix. The sequence of NiAl, Ni2Al3 and NiAl3 intermetallic phases formation was observed. In particular, the morphology of the NiAl3 phase, growing in thin dendrites into the Al matrix, is suitable for the closing of cracks, which pass through the material. [ABSTRACT FROM AUTHOR]