ABSTRACT Polyethylene glycol grafted calcium alginate hydrogel microspheres are synthesized by ring-opening and addition reaction of epoxy chloropropane. FTIR, 13C NMR, optical microscope, SEM, TG, and DSC are used for characterization. Swelling behaviors are studied and it is found that polyethylene glycol grafted calcium alginate microspheres are improved in anti-swelling properties. Protein-imprinted polyethylene glycol grafted calcium alginate hydrogel microspheres exhibit enhanced specific rebinding quantity (11.16 mg/g) and selective recognition properties (4.71 against BHb), towards target molecule in the presence of competing protein, compared with that of the unmodified samples (4.96 mg/g and 1.75, respectively). © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43617. [ABSTRACT FROM AUTHOR]

Vinyl group capped urethane acrylate (UA) was prepared with diisocyanate (IPDI), hydroxyethyl methacrylate (HEMA) and dimethylolpropionic acid (DMPA). The UA was grafted onto sodium alginate via free-radical polymerization with KPS/Na 2 SO 3 as initiator and then crosslinked by Ca 2+ . Grafted polymers (UA- g- CaA) were characterized by FT-IR, SEM, TGA, XRD and tension gauge. The swelling behavior was also investigated. It is found that urethane acrylate grafted calcium alginate possesses lower swelling degree and is improved in thermal stability as well as mechanical performance. The reason is that hydrophobic urethane acrylate provides alginate with physical crosslinking and forms partial crystal regions. The optimum condition for synthesis of UA- g- CaA with lower swelling degree is that weight percentage of initiator to monomer is 0.8%, mass ratio of reductant to oxidant is 0.45:1, monomer concentration is 0.0385 mol/L and grafting reaction temperature is 55 °C. [ABSTRACT FROM AUTHOR]

Abstract: Polyurethane was synthesized by the reaction of isophorone diisocyanate, 2-hydroxyethyl methacrylate and diethylene glycol. Then polyurethane grafted calcium alginate gel material was prepared via free-radical grafting polymerization with azobisisobutyronitrile as an initiator. Modified calcium alginate hydrogel was improved in thermal property, crystallinity and anti-swelling properties. The reason is that polyurethane side chains affect the arrangement of calcium alginate by forming highly ordered crystal region. [Copyright &y& Elsevier]