Roychand, Rajeev, Kilmartin-Lynch, Shannon, Saberian, Mohammad, Li, Jie, Zhang, Guomin, and Li, Chun Qing
The decomposition of organic waste going to landfills produces methane gas, which is 21 times worse than CO 2 in its global warming potential. Spent coffee grounds (SCG) are one type of organic waste that makes up a significant proportion of the organic waste going to landfills. Therefore, it becomes imperative to look for a recycling solution to transform this waste into a valuable resource. The concrete industry has the potential to contribute significantly to increasing the recycling rate of this waste material. However, due to its high organic content, it is unsuitable to be used directly in structural concrete. Therefore, this experimental project looks at pyrolysing this waste at different temperatures (350 and 500 °C) to identify its suitability in improving the physicochemical and mechanical properties of concrete. The raw and pyrolysed forms of SCG were used as a replacement of fine aggregates (FA; sand) at 5, 10, 15 and 20% volume replacement levels. X-ray fluorescence (XRF), Carbon, Hydrogen, Nitrogen, and Sulfur (CHNS) analysis, laser diffraction particle size analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM) and compressive strength tests were undertaken to investigate the properties of the raw material and their performance in the blended concrete composites. The results show that the leaching of organic compounds from the SCG hinders the hydration reaction of cement particles, thereby significantly hampering the compressive strength of SCG-blended concrete. However, pyrolysing the SCG at 350 °C led to a significant improvement in its material properties, which resulted in a 29.3% enhancement in the compressive strength of the composite concrete blended with coffee biochar. [Display omitted] • Spent coffee grounds (SCG) leach organic compounds that hinder the hydration reaction and compressive strength of concrete. • SCG pyrolysed at 350 and 500 °C show strong bond formation with the cement matrix. • 15 vol% replacement of sand with pyrolysed SCG at 350 °C provides ∼30% improvement in concrete strength. • 100% of 75,000 tonnes of waste SCG produced in Australia can be utilised in structural concrete. [ABSTRACT FROM AUTHOR]