The novel I 4 -II-IV 2 -VI 7 quaternary diamond-like semiconductors (DLSs), Cu 4 ZnGe 2 S 7 and Cu 4 CdGe 2 S 7 , were prepared from the constituent elemental powders at elevated temperatures. Cu 4 ZnGe 2 S 7 crystallizes in the polar, chiral space group C 2 and adopts the Cu 4 NiSi 2 S 7 structure-type, which can be considered a derivative of the cubic diamond structure. The cadmium analog takes on the Cu 5 Si 2 S 7 structure-type, which is related to the hexagonal diamond structure, and displays polar, Cc space group symmetry. Both compounds contain [Ge 2 S 7 ]6- anions created by corner-sharing GeS 4 tetrahedra. The crystal structures were carefully evaluated using: 1) extended connectivity tables, 2) minimum bounding ellipsoid analysis, and 3) bond valence sum (BVS) and global instability index (G) calculations. Both compounds are thermally stable up to temperatures exceeding 950 °C and melt incongruently. As assessed using diffuse reflectance spectroscopy, Cu 4 ZnGe 2 S 7 and Cu 4 CdGe 2 S 7 possess optical bandgaps of 1.65 eV and 1.90 eV, respectively, which are narrower than the analogous I 2 -II-IV-VI 4 DLSs. Electronic structure calculations show that both compounds are direct-bandgap semiconductors with significant contributions of Cu- d and S- p orbitals to the states at the top of the valence band. While Cu 4 CdGe 2 S 7 displays a weak second harmonic generation (SHG) response, the second-order nonlinear optical susceptibility, χ(2), of Cu 4 ZnGe 2 S 7 is 14.8 ± 1.5 pm V-1, assessed using the Kurtz-Perry powder method and an optical-grade AgGaSe 2 (AGSe) reference. Both compounds exhibit laser-induced damage threshold values similar to AGSe, ∼0.1 GW cm-2, for λ = 1.064 µm using picosecond laser pulses. Most importantly, Cu 4 ZnGe 2 S 7 exhibits a phase-matching behavior at λ = 3.1 µm. These results suggest that Cu 4 ZnGe 2 S 7 holds potential for use in low-powered laser applications involving efficient wave mixing in the mid-IR region. [Display omitted] • Cu 4 ZnGe 2 S 7 is a novel diamond-like material with the Cu 4 NiSi 2 S 7 structure type. • Cu 4 CdGe 2 S 7 is a novel diamond-like material with the Cu 5 Si 2 S 7 structure type. • Optical bandgaps of Cu 4 ZnGe 2 S 7 and Cu 4 CdGe 2 S 7 are 1.65 and 1.90 eV, respectively. • Cu 4 ZnGe 2 S 7 has χ (2) value of 14.8 ± 1.5 pm V− 1 and is phase matching for λ = 3.1 µm. • Cu 4 ZnGe 2 S 7 is a candidate for low-powered laser applications in the mid-IR region. [ABSTRACT FROM AUTHOR]