Abstract: In this paper, single crystal of ytterbium (Yb) doped Ca5(PO4)3F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (σ abs) is 5.117×10−20 cm2 with an FWHM of 4nm at 982nm. The emission cross-section (σ em) is 3.678×10−20 cm2 at 1042nm. Favorable values of the absorption cross-section at about 982nm are promising candidates for laser diode (LD) pumping. [Copyright &y& Elsevier]

Abstract: A large and transparent Yb:FAP crystal with dimensions up to ∅30mm×85mm has been grown by the Czochralski method. The preparation of the raw material has been investigated. X-ray power diffraction studies of Yb:FAP crystal confirm that the as-grown crystal is isostructural with the FAP crystal. The crystalline quality has been studied using X-ray rocking curve analysis. The segregation coefficient of Yb3+ in the Yb:FAP crystal has been also determined. Linear thermal expansion coefficients in [001] and [100] directions have been measured in the 30–800°C temperature range. [Copyright &y& Elsevier]

Tb 3+ -doped YAlO 3 (YAP) single crystal was grown by Czochralski (Cz) method. Based on the polarized absorption spectra, the spectroscopic parameters were calculated to be Ω 2 = 3.49 × 10 −20 cm 2 , Ω 4 = 5.87 × 10 −20 cm 2 and Ω 6 = 2.55 × 10 −20 cm 2 , and then the spontaneous transition rate, fluorescent branching ratio and radiative lifetime of 5 D 4 multiplet were obtained. The yellow emission cross sections of 5 D 4 → 7 F 4 transition were calculated to be 1.72 × 10 −22 cm 2 , 2.73 × 10 −22 cm 2 and 2.65 × 10 −22 cm 2 for a, b and c polarization, respectively. The fluorescence lifetime of the 5 D 4 multiplet was fitted to be 1.72 ms. All the data indicate that Tb:YAP crystal is a promising candidate for yellow laser operation. [ABSTRACT FROM AUTHOR]