Search

In this study, an investigation of the shear behavior of full-scale reinforced concrete (RC) beams affected from alkali–silica reactivity damage is presented. A detailed finite element model (FEM) was developed and validated with data obtained from the experiments using several metrics, including a force–deformation curve, rebar strains, and crack maps and width. The validated FEM was used in a parametric study to investigate the potential impact of alkali–silica reactivity (ASR) degradation on the shear capacity of the beam. Degradations of concrete mechanical properties were correlated with ASR expansion using material test data and implemented in the FEM for different expansions. The finite element (FE) analysis provided a better understanding of the failure mechanism of ASR-affected RC beam and degradation in the capacity as a function of the ASR expansion. The parametric study using the FEM showed 6%, 19%, and 25% reduction in the shear capacity of the beam, respectively, affected from 0.2%, 0.4%, and 0.6% of ASR-induced expansion.

This paper investigates the dynamic characteristics of a multilevel structure for the transportation and storage of spent nuclear fuel (SNF) from commercial power plants. The nuclear fuel is stored in slender rods that are grouped together into fuel assemblies (FA). In a sealed cylindrical container called “canister”, the FA are inserted into a honeycomb basket. The objective of this paper is to develop a computational model that accurately represents the structural dynamics of the canister as seen from its external surface, such that this computational model can be used in the context of structural integrity assessment of the internal components (FA and fuel rods) based on external vibration measurements. The numerous components lead to a large finite element model, and correspondingly, vibration modes and eigenfrequencies. Nevertheless, the localized connections between components enable an efficient domain decomposition with few interface coordinates. Craig–Bampton (CB) substructuring is thus used to perform the modal analysis. However, the high modal density yields a large-scale CB eigenvalue problem that necessitates a sparse solver. A block factorization by Schur complement that exploits the sparsity of the CB matrices allows an efficient calculation of the numerous eigenpairs. Many local vibration modes contribute little to the dynamics of the SNF canister. The main contribution of this paper is the development of an efficient methodology for determining the importance of each of the substructural modes of the CB model. The removal of the least dominant substructural modes allows for reducing the CB model. Using a 75% filtering, a significant speed-up is obtained, without noticeable loss of accuracy.

This study focuses on two separate investigations of the main aging mechanisms: alkali&ndash, silica reactivity (ASR) and the corrosion of reinforcing steel (rebar) concrete, both of which may result in a premature failure to meet the serviceability or strength requirements of a concrete structure. However, these processes occur very slowly, spanning decades. The impact of direct chemical additives to fresh concrete to accelerate ASR and the corrosion of reinforcing steel on the fresh and hardened properties of the ensuing material are investigated to inform the potential use of chemicals in large-scale studies. The deterioration of reinforced concrete (RC) is determined by means of expansion, cracking, bulk diffusivity and surface resistivity measurements, and compressive, split tensile and flexural strength tests. The results indicate that the addition of sodium hydroxide and calcium chloride can effectively accelerate the crack formation and propagation in concrete due to ASR and the corrosion of rebar, respectively. The ASR-induced cracks maintained a constant crack width from 0.05 mm to 0.1 mm over the measurement period regardless of the intensity of aging acceleration. Adding 4% chloride by weight of cement for accelerating rebar corrosion resulted in an average crack that was 82% larger than in the case of ASR accelerated with the addition of sodium hydroxide. The addition of alkali resulted in an increase in early-age (7-day) strength. At a total alkali loading of 2.98 kg/m3, 3.84 kg/m3 and 5.57 kg/m3, the 28-day compressive strength of concrete decreased by 3%, 10% and 24%, respectively. Similarly, a higher early-age strength and a lower later-age strength was observed for the concrete in the presence of corrosive calcium chloride. The results from this research are expected to inform future studies on the long-term performance of RC structures under accelerated ASR and corrosion.

Advancement in material science has enabled the engineers to enhance the strength and long-term behavior of concrete structures. The conventional approach is to use steel for prestressed bridge girders. Despite having good ductility and strength, beams prestressed with steel are susceptible to corrosion when subjected to environmental exposure. The corrosion of the prestressing steel reduces load carrying capacity of the prestressed member and result in catastrophic failures. In the last decades, more durable composite materials such as Aramid Fiber Reinforced Polymer (AFRP), Glass Fiber Reinforced Polymer (GFRP) and Carbon Fiber Reinforced Polymer (CFRP) have been implemented in concrete structures as a solution to this problem. Among these materials, CFRP stands out as a primary prestressing reinforcement, which has the potential to replace steel and provide corrosion free prestressed bridge girders. Despite its promise, prestressing CFRP has not frequently been used for bridge construction worldwide. The major contributing factor to the lack of advancement of this promising technology in the United States (U.S.) is the lack of comprehensive design specifications. Apart from a limited number of guides, manuals, and commentaries, there is currently no standard or comprehensive design guideline available to bridge engineers in the U.S. for the design of concrete structures prestressed with CFRP systems. The main goal is to develop design guidelines in AASHTO-LRFD format for concrete bridge girders with prestressing CFRP materials. The guidelines are intended to address the limitation in current AASHTO-LRFD Bridge Design Specifications which is applicable for prestressed bridge girders with steel strands. To accomplish this goal, some of the critical parameters that affect the design and long-term behavior of prestressed concrete bridge girders with prestressing CFRP systems are identified and included in the research work. This paper presents preliminary results of an experimental study that is part of a National Highway Co-operative Highway Research Program (NCHRP) project.

Although concrete is a noncombustible material, high temperatures such as those experienced during a fire have a negative effect on the mechanical properties. This paper studies the effect of elevated temperatures on the mechanical properties of limestone, quartzite and granite concrete. Samples from three different concrete mixes with limestone, quartzite and granite coarse aggregates were prepared. The test samples were subjected to temperatures ranging from 25 to 650 °C for a duration of 2 h. Mechanical properties of concrete including the compressive and tensile strength, modulus of elasticity, and ultimate strain in compression were obtained. Effects of temperature on resistance to degradation, thermal expansion and phase compositions of the aggregates were investigated. The results indicated that the mechanical properties of concrete are largely affected from elevated temperatures and the type of coarse aggregate used. The compressive and split tensile strength, and modulus of elasticity decreased with increasing temperature, while the ultimate strain in compression increased. Concrete made of granite coarse aggregate showed higher mechanical properties at all temperatures, followed by quartzite and limestone concretes. In addition to decomposition of cement paste, the imparity in thermal expansion behavior between cement paste and aggregates, and degradation and phase decomposition (and/or transition) of aggregates under high temperature were considered as main factors impacting the mechanical properties of concrete. The novelty of this research stems from the fact that three different aggregate types are comparatively evaluated, mechanisms are systemically analyzed, and empirical relationships are established to predict the residual compressive and tensile strength, elastic modulus, and ultimate compressive strain for concretes subjected to high temperatures.