Search

This article investigates the influence of NaPF6 salt content (0–30 wt.% in a varying interval of 5 wt.%) on the structural, electrical, and biodegradable properties of HEC/NaPF6 solid biopolymer electrolyte (SBE) films. The interaction of salt with the HEC polymer matrix is confirmed by FTIR and SEM studies. The elemental composition and mapping confirm the appearance of NaPF6 moieties in the HEC polymer matrix. XRD deconvolution reveals that HEC samples with 20 wt.% (H4) and 10 wt.% of salt (H2) have a significantly lower crystallinity index than pure HEC polymer. The H2 and H4 samples show the highest room temperature conductivity values (1.62 × 10−5 and 1.13 × 10−5 S cm−1, respectively) among all other prepared samples since carrier concentration influences the ionic conductivity and shares a similar order of conductivity. Thus, the H2 and H4 samples are employed as electrolyte separators in the sodium ion battery, and the results suggest that the H2‐based electrolyte system is more significant. Battery matrices like open circuit voltage (V), current density (μA cm−2), power density (mW kg−1), energy density (Wh kg−1) and discharge capacity (μA h−1) were calculated and found to be 2.48, 5.49, 44.60, 1.69, and 71.05, respectively for H2 electrolyte based cell. Wagner polarization reveals that H2 and H4 constitute the predominant charge carriers (ions) with total ion transference numbers of ⁓0.98 and ⁓0.99, respectively. To evaluate sample degradability, H2 and H4 samples were subjected to 20 and 5‐day biodegradation processes, during which the polymers completely (100%) broke down. [ABSTRACT FROM AUTHOR]

The increased interest in the transition from liquid to solid polymer electrolytes (SPEs) has driven enormous research in the area polymer electrolyte technology. Solid biopolymer electrolytes (SBEs) are a special class of SPEs that are obtained from natural polymers. Recently, SBEs have been generating much attention because they are simple, inexpensive, and environmentally friendly. In this work, SBEs based on glycerol-plasticized methylcellulose/pectin/potassium phosphate (MC/PC/K3PO4) are investigated for their potential application in an electrochemical double-layer capacitor (EDLC). The structural, electrical, thermal, dielectric, and energy moduli of the SBEs were analyzed via X-ray diffractometry (XRD), Fourier transforms infrared spectroscopy (FTIR), electrochemical impedance spectroscopy (EIS), transference number measurement (TNM), and linear sweep voltammetry (LSV). The plasticizing effect of glycerol in the MC/PC/K3PO4/glycerol system was confirmed by the change in the intensity of the samples' FTIR absorption bands. The broadening of the XRD peaks demonstrates that the amorphous component of SBEs increases with increasing glycerol concentration, while EIS plots demonstrate an increase in ionic conductivity with increasing plasticizer content owing to the formation of charge-transfer complexes and the expansion of amorphous domains in polymer electrolytes (PEs). The sample containing 50% glycerol has a maximal ionic conductivity of about 7.5 × 10−4 scm−1, a broad potential window of 3.99 V, and a cation transference number of 0.959 at room temperature. Using the cyclic voltammetry (CV) test, the EDLC constructed from the sample with the highest conductivity revealed a capacitive characteristic. At 5 mVs−1, a leaf-shaped profile with a specific capacitance of 57.14 Fg−1 was measured based on the CV data. [ABSTRACT FROM AUTHOR]

In this present work, we have synthesized silver nanoparticles (AgNPs) using the chemical reduction method and systematically studied the effect of AgNPs of different loading into polyvinyl alcohol/sodium bromide (PVA/NaBr) polymer electrolytes. X‐ray diffraction and Fourier transform infrared spectroscopy confirmed the variation in the crystallinity and complexation with AgNPs loading, respectively. AgNPs are uniformly distributed in the polymer matrix as depicted in FESEM. According to transport property studies, it is observed that carrier concentration has a strong influence on ionic conductivity. Additionally, I‐t studies showed that most charge carriers are ions and not electrons. The sample PVA/NaBr with AgNPs, prepared from 6 mM AgNO3 solution (PNAg6) with ionic conductivity 1.22 × 10−4 S cm−1 (one order increase with respect to undoped sample) and highest electrochemical stability window (ESW) of 2.86 V, can be chosen as a suitable candidate for energy storage device applications. [ABSTRACT FROM AUTHOR]