Search

The design of an active, stable and efficient photocatalyst that is able to be used for hydrogen production is of great interest nowadays. Therefore, four methods of AgTaO3 perovskite synthesis, such as hydrothermal, solvothermal, sol-gel and solid state reactions, were proposed in this study to identify the one with the highest hydrogen generation efficiency by the water splitting reaction. The comprehensive results clearly show that the solid state reaction (SSR) led to the obtainment of a sample with an almost seven times higher photocatalytic activity than the other methods. Furthermore, four ionic liquids, all possessing nitrogen in the form of organic cations (two imidazoliums with different anions, ammonium and tetrazolium), were used for the first time to prepare composites consisting of AgTaO3 modified with IL and Pt, simultaneously. The effect of the ionic liquids (ILs) and Pt nanoparticles&rsquo, presence on the structure, morphology, optical properties, elemental composition and the effectiveness of the hydrogen generation was investigated and discussed. The morphology investigation revealed that the AgTaO3 photocatalysts with the application of [OMIM]-cation based ILs created smaller granules (&lt, 500 nm), whereas [TBA] [Cl] and [TPTZ] [Cl] ILs caused the formation of larger particles (up to 2 &mu, m). We found that various ILs used for the synthesis did not improve the photocatalytic activity of the obtained samples in comparison with pristine AgTaO3. It was detected that the compound with the highest ability for hydrogen generation under UV-Vis irradiation was the AgTaO3_0.2% Pt (248.5 &mu, mol∙g&minus, 1), having an almost 13 times higher efficiency in comparison with the non-modified pristine sample. It is evidenced that the enhanced photocatalytic activity of modified composites originated mainly from the presence of the platinum particles. The mechanism of photocatalytic H2 production under UV-Vis light irradiation in the presence of an AgTaO3_IL_Pt composite in the water splitting reaction was also proposed.

Spherical microparticles of TiO2 were synthesized by the ionic liquid-assisted solvothermal method at different reaction times (3, 6, 12, and 24 h). The properties of the prepared photocatalysts were investigated by means of UV-VIS diffuse-reflectance spectroscopy (DRS), Brunauer&ndash, Emmett&ndash, Teller (BET) surface area measurements, scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), and X-ray photoelectron spectroscopy (XPS). The results indicated that the efficiency of the phenol degradation was related to the time of the solvothermal synthesis, as determined for the TiO2_EAN(1:1)_24h sample. The microparticles of TiO2_EAN(1:1)_3h that formed during only 3 h of the synthesis time revealed a really high photoactivity under visible irradiation (75%). This value increased to 80% and 82% after 12 h and 24 h, respectively. The photoactivity increase was accompanied by the increase of the specific surface area, thus the poresize as well as the ability to absorb UV-VIS irradiation. The high efficiency of the phenol degradation of the ionic liquid (IL)&ndash, TiO2 photocatalysts was ascribed to the interaction between the surface of the TiO2 and ionic liquid components (carbon and nitrogen).

A series of novel BiyXz-TiO2/SrTiO3 composites were prepared by multistep synthesis route. The as-prepared photocatalysts were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), diffuse reflectance spectroscopy (DRS), Fourier transform infrared (FT-IR), Raman spectra and BET analysis. The photocatalytic activity test was performed in aqueous solution of phenol under the irradiation of visible light range (λ ≥ 420 nm). Obtained results revealed that the BiOI_TiO2/SrTiO3 sample exhibit the highest photocatalytic activity under visible irradiation (0.6 μmol/dm3/min). Thus, it was demonstrated that modification of the TiO2/SrTiO3 microspheres by flowers-like structure made of bismuth oxyiodide resulted in enhancement of photocatalytic activity under visible light. The role of active species during the decomposition process of organic compound was investigated using different types of active species scavengers as well as electron paramagnetic resonance analysis (EPR). The study showed that in the BiOI_TiO2/SrTiO3/Vis system the holes (h+) plays relevant role in phenol decomposition. Furthermore, the stability and recyclable properties of obtained BiOI_TiO2/SrTiO3 sample were confirmed during three consecutive processes.

Because of the tremendous structural diversity of ionic liquids (ILs), simple transfer of observations performed for one IL used for IL-TiO2 preparation on different samples is not possible. Therefore, four ionic liquids, all containing distinct nitrogen-bearing organic cations (pyridinium, pyrrolidinium, ammonium, imidazolium), were used for the first time for the preparation of IL-TiO2 composites. The role of the individual IL cation in the synthesis of TiO2 microspheres, as well as the effect of the IL structure on the mechanism of the visible-light (Vis)-induced photoactivity of IL-TiO2 was presented and discussed in regard to structure, morphology, absorption properties, elemental composition, and reactive species involved in the photocatalytic reaction of phenol degradation. The successful modification of the TiO2 with organic IL species including possible interactions between IL and TiO2 surface, as well as the TiO2 matrix (doping with N), were confirmed. The sample that exhibited the highest photo...