Search

Incineration is currently the standard way of disposing of municipal waste. It uses components protected by high-temperature-resistant layers of materials, such as Inconel alloys. Therefore, the objective of the current paper is to study the mechanical properties and structure of a bimetallic Inconel 625-16Mo3 steel tube. The Inconel 625 layer was 3.5 mm thick and was applied to the surface of the tube with a wall thickness of 7 mm via the cold metal transfer method. The bimetallic tube was bent using a supercritical bend (d ≤ 0.7D). This paper is focused on the investigation of the material changes in the Inconel 625 layer areas influenced by the maximum tensile and compressive stresses after the bend. The change in layer thickness after the bend was evaluated and compared to the non-deformed tube. In addition, the local mechanical properties (nanohardness, Young modulus) across the indicated interfacial areas using quasistatic nanoindentation were investigated. Subsequently, a thorough microstructure observation was carried out in areas with maximum tensile and compressive stresses to determine changes in the morphology and size of dendrites related to the effect of tensile or compressive stresses induced by bending. It was found that the grain featured a stretched secondary dendrite axis in the area of tensile stress, but compressive stress imparted a prolongation of the primary dendrite axis.

Custom 450 stainless steel is the most desirable material across industries due to its widespread application in the aerospace, defense and marine industries. Stainless-steel materials are challenging to deal with and fall into the list of hard-to-process materials due to their low heat conduction coefficient and high mechanical properties. In this research work, end milling was carried out on Custom 450 stainless steel machined using TiAlN coated with tungsten carbide inserts that have been cryo-treated (CT) for 24 h (24 h) and 36 h (36 h), as well as untreated (UT) inserts. The inserts were evaluated in terms of feed force, feed rate and consistent depth of cut (ap) at various spindle speeds (S). Also examined were the tool morphology, chip anatomy and surface morphology of cryo-treated material compared to untreated inserts at various responses to cutting force (Fx, Fy, Fz), cutting temperature (Tc), vibration and surface abrasion. For inserts that have been cryo-treated for 36 h, the feed force (Fx) value was 44% and 5% less compared to inserts treated for 24 h and in UT inserts, respectively. Furthermore, for 24-h and 36-h CT inserts, feed force (Fx) was 12% and 20% less compared to a UT insert. Using 24-h cryo-treated inserts as opposed to UT inserts significantly reduced the surface roughness by 20%. Cutting inserts that have undergone cryogenic treatment have been observed to exhibit longer cutting tool life due to less wear and friction on the cutting edges.

The paper presents and discusses questions on structure formation during the sintering process of Cr 2 O 3 -based composites using the hot pressing method, when a chemical reaction between the components takes place. The task was difficult because Cr 2 O 3 decomposes when sintered at temperatures above 1300 °C. The proposed novel method allowed for interaction between aluminum and chromia, thus avoiding the decomposition of the latter. Here, ultrafine aluminum powder played the role of the active agent forming a liquid phase and reacting with Cr 2 O 3 . The appearance of the solid solutions of (Cr,Al) 2 O 3 with different stoichiometry of Cr and Al depended on the aluminum content in the initial mixture. The solid solution significantly strengthened boundaries between composite phases, resulting in the composite material of high fracture toughness between 5 and 7 MPa m ½ and bending strength of ca. 500 MPa. The best mechanical properties exhibited the cermet with 22 wt.% of the restored chromium.

The 17 O isotopomer of the water-endofullerene H 2 O@C 60 displays a remarkable proton NMR spectrum, with six well resolved peaks. These peaks are due to the J-coupling between the water protons and the 17 O nucleus, which has spin-5/2. The resolution of these peaks is enabled by the suppression of water proton exchange by the fullerene cage. The six peaks display an unusual pattern of linewidths, which we model by a Liouville-space treatment of scalar relaxation due to quadrupolar relaxation of the 17 O nuclei. The data are consistent with rotational diffusion of the water molecules on the sub-picosecond timescale., (© 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.)