Search

In this work, macro- and nanodiagnostic procedures for working, third-generation photovoltaic devices based on a modified polymer:fullerene (P3HT:PCBM) absorber were conducted using atomic force microscopy (AFM) and impedance spectroscopy (IS) equipment. All experiments were performed both in the dark and under irradiation with a specific light wavelength. Photoactive Kelvin probe force microscopy (p-KPFM) and impedance spectroscopy (p-IS) experiments were conducted on half- and whole-solar cell devices. Based on the p-KPFM measurements, the surface potential (SP) and surface photovoltage (SPV) on top of the active layer at the micro/nanoscale were estimated for various light wavelengths (red, green, blue, and white). For light in the red spectrum range, which was associated with an optical absorption edge and acceptor states that occurred in the band gap of the P3HT material after doping the donor polymer with iodine, the SPV was measured at levels of 183 mV, 199 mV, and 187 mV for the samples with 0%, 5% and 10% iodine doping, respectively. In addition, a macroscale investigation enabling the determination of the electrical parameters of the studied organic solar cells (OSCs) was carried out using p-IS. Based on the data obtained during p-IS experiments, it was possible to propose a series electrical equivalent circuit to define and describe the charge transfer phenomenon in the OSCs. Estimations of data obtained from the fitting of the experimental results of p-IS under white light allowed us to evaluate the average diffusion time of electric charges at 8.15 µs, 16.66 µs, and 24.15 µs as a function of organic layer thickness for the device without doping and with 5% and 10% iodine doping. In this study, we demonstrated that correlating information obtained at the macro- and nanoscale enabled a better understanding of the electrical charge distribution of OSCs for indoor applications. [ABSTRACT FROM AUTHOR]

Electrochromism of organic compounds is a well-known phenomenon; however, nowadays, most research is focused on anodic coloring materials. Development of efficient, cathodic electrochromic materials is challenging due to the worse stability of electron accepting materials compared with electron donating ones. Nevertheless, designing stable cathodic coloring organic materials is highly desired—among other reasons—to increase the coloration performance. Hence, four phthalimide derivatives named 1,5-PhDI, 1,4-PhDI, 2,6-PhDI and 3,3′-PhDI were synthesized and analyzed in depth. In all cases, two imide groups were connected via naphthalene (1,5-PhDI, 1,4-PhDI, 2,6-PhDI) or 3,3′-dimethylnaphtidin (3,3′-PhDI) bridge. To observe the effect of chemical structure on physicochemical properties, various positions of imide bond were considered, namely, 1,5- 1,4- and 2,6-. Additionally, a compound with the pyromellitic diimide unit capped with two 1-naphtalene substituents was obtained. All compounds were studied in terms of their thermal behavior, using differential calorimetry (DSC) and thermogravimetric analysis (TGA). Moreover, electrochemical (CV, DPV) and spectroelectrochemical (UV–Vis and EPR) analyses were performed to evaluate the obtained materials in terms of their application as cathodic electrochromic materials. All obtained materials undergo reversible electrochemical reduction which leads to changes in their optical properties. In the case of imide derivatives, absorption bands related to both reduced and neutral forms are located in the UV region. However, importantly, the introduction of the 3,3′-dimethylnaphtidine bridge leads to a noticeable bathochromic shift of the reduced form absorption band of 3,3′-PhDI. This indicates that optimization of the phthalimide structure allows us to obtain stable, cathodic electrochromic materials. [ABSTRACT FROM AUTHOR]

In this study, lithium borohydride (LiBH4) reduction was used to modify the surface chemistry of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) fibers. Although the most common reaction employed in the surface treatment of polyester materials is hydrolysis, it is not suitable for fiber modification of bacterial polyesters, which are highly resistant to this type of reaction. The use of LiBH4 allowed the formation of surface hydroxyl groups under very mild conditions, which was crucial for maintaining the fibers' integrity. The presence of these groups resulted in a noticeable improvement in the surface hydrophilicity of PHBV, as revealed by contact angle measurements. After the treatment with a LiBH4 solution, the electrospun PHBV fibrous mat had a significantly greater number of viable osteoblast-like cells (SaOS-2 cell line) than the untreated mat. Moreover, the results of the cell proliferation measurements correlated well with the observed cell morphology. The most flattened SaOS-2 cells were found on the surface that supported the best cell attachment. Most importantly, the results of our study indicated that the degree of surface modification could be controlled by changing the degradation time and concentration of the borohydride solution. This was of great importance since it allowed optimization of the surface properties to achieve the highest cell-proliferation capacity. [ABSTRACT FROM AUTHOR]

Three new azomethines based on triphenylamine with two or three substituents were obtained. Chemical structure and purity were confirmed by 1H NMR, FTIR elemental analysis and mass spectroscopy. The investigations were focused on the relationship between chemical structure and properties important for optoelectronic materials. Thus, the studies of thermal, optical and electrochemical properties were carried out based on differential scanning calorimetry, thermogravimetric analysis, electronic absorption, photoluminescence and cyclic voltammetry measurements. The ongoing consideration of experimental results was complemented by theoretical calculations using the density functional theory method. The donor activity of obtained compounds was tested in bulk-heterojuntion photovoltaic cells with structure ITO/PEDOT:PSS/imine:PCBM/Al and ITO/PEDOT:PSS/imine:P3HT:PCBM/Al). The effect of the presence of the amino-thiophene-3,4-dicarboxylic acid diethyl ester groups and various number of hexyloxyphenyl units on imines properties was demonstrated. [ABSTRACT FROM AUTHOR]

The paper presents synthesis and characterization of nine new thiazolyl-(phenyldiazenyl)-2H-chromen-2-one dyes. The impact of substituent structure in thiazole ring in the synthesized azocoumarin derivatives on electrochemical properties, photoisomerization process and photovoltaic response was examined. The dyes were electrochemically active and undergo reduction and oxidation processes. They showed low electrochemically estimated energy band gap in the range of 1.71–2.13 eV. Photoisomerization process of the synthesized molecules was studied in various solvents such as ethanol, chloroform and N,N-dimethylformamide (DMF) upon the UV illumination. It was found that novel azodyes showed reversible trans-cis-trans isomerization and exhibited long thermal back to the trans form, that was even 7 days in DMF. Selected azocoumarin were molecularly dispersed in polystyrene for preparation of guest-host azopolymer systems to study the cis-trans thermal isomerization of obtained dyes in solid state. The photovoltaic activity of the azochromophores was tested in bulk-heterojunction solar cells. They acting as weak donors in device with structure ITO/PEDOT:PSS/dye:PC70BM/Al. No photovoltaic response of cells with azocoumarin derivatives bearing 4-fluorobenzene, 3,4-dichlorobenzene, or 4-(1-adamantyl) unit was found. Additionally, dye which showed the best activity was examined in three-component solar cells ITO/PEDOT:PSS/PTB7:PC70BM:dye/PFN/Al. [ABSTRACT FROM AUTHOR]

ABSTRACT: Optical properties of polymer/fullerene blend films upon thermal annealing are investigated by spectroscopic ellipsometry and described consistently within an optical model of the blend film. The optical model developed in this work treats both components, polymer and fullerene, as mixtures of reference materials, that is, their optically ordered and disordered phase. Then, the polymer/fullerene blend layer is also described as a mixture of these two components. In this manner, we extend an existing optical model, which accounts for the optical order within the polymer phases, on cases where the optically ordered PCBM phase occurs, too. Determination of the dielectric functions of all four reference materials allows for a unique quantitative characterization of a polymer/fullerene blend film by assigning to it thickness and the polymer to fullerene volume fraction of its layers as well as corresponding volume fractions of theirs optically ordered and disordered polymer and fullerene phases. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2018, 56, 1094–1100 [ABSTRACT FROM AUTHOR]

Optical and structural properties of a blend thin film of (1:1 wt.) of poly(3-hexylthiophene) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) doped with iodine (I2) and then exposed to a stepwise heating were reported and compared with the properties of doped P3HT films. The UV-Vis(T) absorption measurements were performed in situ during annealing runs, at the precisely defined temperatures, in a range of 20–210 °C. It was demonstrated that this new method allows one to observe the changes of absorption spectra, connected with the iodine release and other structural processes upon annealing. In addition, the thermally-induced changes of the exciton bandwidth (W) and the absorption edge parameters, i.e., the energy gap (EG) and the Urbach energy (EU) were discussed in the context of different length of conjugation and the structural disorder in polymers and blends films. During annealing, several stages were distinguished and related to the following processes as: the iodine escape and an increase in P3HT crystallinity, the orderly stacking of polymer chains, the thermally inducted structural defects and the phase separation caused by an aggregation of PCBM in the polymer matrix. Moreover, the detailed X-ray diffraction studies, performed for P3HT and P3HT:PCBM films, before and after doping and then after their thermal treatment, allowed us to consider the structural changes of polymer and blend films. The effect of iodine content and the annealing process on the bulk heterojunction (BHJ) solar cells parameters was checked, by the impedance spectroscopy (IS) measurements and the J-V characteristics registration. All of the investigated P3HT:PCBM blend films showed the photovoltaic effect; the increase in power conversion efficiency (PCE) upon iodine doping was demonstrated. [ABSTRACT FROM AUTHOR]

Three novel conjugated polyazomethines have been obtained by polycondensation of diamines consisting of the diimine system, with either 2,5-bis(octyloxy)terephthalaldehyde or 9-(2-ethylhexyl)carbazole-3,6-dicarboxaldehyde. Partial replacement of bulky solubilizing substituents with the smaller side groups has allowed to investigate the effect of supramolecular organization. All obtained compounds have been subsequently identified using the NMR and FTIR spectroscopies and characterized by the thermogravimetric analysis, differential scanning calorimetry, cyclic voltammetry, UV–Vis spectroscopy, and X-ray diffraction. Investigated polymers have shown a good thermal stability and high glass transition temperatures. X-ray measurements have proven that partial replacement of octyloxy side chains with smaller methoxy groups induced a better planarization of macromolecule. Such modification has tuned the LUMO level of this molecule and caused a bathochromic shift of the lowest energy absorption band. On the contrary, imines consisting of N-ethylhexyl substituted carbazole units have not been so clearly affected by alkyl chain length modification. Photovoltaic activity of imines (acting as a donor) in bulk-heterojunction systems has been observed for almost all studied compounds, blended with the fullerene derivative (PCBM) in various weight ratios. [ABSTRACT FROM AUTHOR]

Three polyazomethines and their corresponding model compounds were protonated with trifluoroacetic acid, and its effect on their optical (UV-vis absorption and photoluminescence) properties and electrochemical behavior has been studied, in the context of the presence and elongation of alkoxy side groups. Moreover, the effect of environment dielectric constants (i.e., polarity of the solvent) was considered on the doping process. It has been proven that the presence of alkoxy side groups is necessary for protonation to occur, while unsubstituted compounds undergo hydrolysis to constitutive units. Acid doping of imines consisting of alkoxy side chains has resulted in a distinct bathochromic shift (>200 nm) of the low-energy absorption band. Even the length of alkyl chains has not affected the position of shifted bands; it has been observed that azomethines with smaller, methoxy side groups undergo the protonation process much faster than their octyloxy-substituted analogues, due to the absence of steric hindrance. The electrochemical studies of these alkoxy-substituted imines have indicated a better p-type behavior after protonation induced by the capability of the protonated form to easily oxidize in acetonitrile and to generate the native molecules. The environmental polarity has also had impact on the doping process, which took place only in low-polar media.

In this work we present an in-depth study of the how the composition of poly(3-hexylthiophene) (P3HT):[6,6]-phenyl-C 61 -butyric acid methyl ester (PCBM) blend films influences their phase transitions using variable-temperature spectroscopic ellipsometry. We demonstrate that this non-destructive method is a very sensitive optical technique to investigate the phase transitions and to determine the glass transition temperatures and melting crystallization points of the P3HT:PCBM blend films. By analyzing the influence of the temperature T on the raw ellipsometric data, we have identified a high sensitivity of the ellipsometric angle Δ at a wavelength of 280 nm to temperature changes. Characteristic temperatures determined from the slope changes of the Δ( T ) plot appeared to be very good guess values for the phase transition temperatures.